【摘 要】
：
围绕ＴＩＧ熔修技术提高船体钢焊接接头抗爆性能问题进行了比较全面的试验研究，结果表明，经熔修处理后的４４１ＭＰａ和５８８ＭＰａ级船体钢焊接接头与未熔修相比，其爆炸冲击抗力均有不同程度的改善，其中，尤以４４１ＭＰａ级
论文部分内容阅读
围绕ＴＩＧ熔修技术提高船体钢焊接接头抗爆性能问题进行了比较全面的试验研究，结果表明，经熔修处理后的４４１ＭＰａ和５８８ＭＰａ级船体钢焊接接头与未熔修相比，其爆炸冲击抗力均有不同程度的改善，其中，尤以４４１ＭＰａ级船体钢接头效果最为显著。这对提高舰船生命力和可靠性具有重要的实际意义。
A comparatively comprehensive experimental study on the anti-explosion performance of steel welded joints of hull was carried out with TIG welding technique. The results show that the welded joints of 441MPa and 588MPa hull steel welded after repaired have higher impact strength There are different degrees of improvement, of which, especially 441MPa grade steel hull joint effect is the most significant. This is of great practical significance for enhancing the vitality and reliability of the ship.
其他文献
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
阐述了厚浆型玻璃鳞片涂料的防护机理，并结合化肥厂设备防腐蚀应用实例介绍了两种新型防腐涂料。
The protective mechanism of the thick glass flake coating is expounded
下面举一例说明户籍地与居住地不一致的纳税人如何纳税申报。例:小田是一个自由演员,户籍湖北省武汉市汉口区。2003年初小田到杭州,一年后转到上海并在那里居住了二年。直到2
吉林省会长春,西郊辽阳街7—3号,有栋其貌不扬的二层居民楼,楼内住着6户寻常百姓,还有一个特殊的人家,户主姓张名铁山,故事就从他讲起。 内求团结 张铁山1964年从白城农校毕
近年来随着电子机器不断向高频化的发展，传统使用的软磁铁氧体作为电磁波吸收材料已不能充分发挥其功能，急待开发特别是在１ＧＨｚ以上频率下电磁波吸收特性优良的新材料。通常作为电磁
目的探讨三七皂苷单体Rb1在低氧高二氧化碳性肺动脉收缩(hypoxia hypercapnia-induced pulmonary vasoconstriction,HHPV)中的保护作用及机制。方法原代培养健康雄性SD大鼠肺
习近平总书记于2014年10月15日在北京主持召开了文艺工作座谈会,并发表了重要讲话。当时,我正在延川县关庄与靳之林等老艺术家陪孙立哲等北京知青搞送医下乡活动。一听这消息
在近中性环境中，研究了钡与偶氮胂Ⅲ、锌（钴）、邻菲口罗啉形成多元配合物的条件及其配合物组成。显色体系的摩尔吸光系数由二元配合物的２．１×１０４Ｌ·ｍｏｌ－１·ｃｍ－１提高到７．４×１０４Ｌ·ｍｏｌ－１·ｃｍ－１。用此方法，经过简单的
实施“七七”扶贫攻坚计划,是实现第二步战略目标的重要任务,是解决云南经济发展不平衡的重要途径,也是充分体现社会主义共同富裕的战略性措施,意义非
Implementing the “
王羲之,草书,《壮陶阁续帖》子册,五行四十九字.rn[释文]rn秋深感怀.但有慨叹.得书/(知)足下当至洛.不能就彼/举聚.事势复之行以/释然不.吾故劣劣.近粗平安./甚忧(卿).还具示