本文研究了Ni-P化学镀A_(587)CL_1在人工海水溶液中的腐蚀疲劳寿命。结果表明,在不同疲劳载荷和不同频率下,镀层提高了试样的腐蚀疲劳寿命,在343MPa应力和0.3Hz频率时,提高到
【机 构】
：
中国科学院金属研究所,中国科学院金属研究所 沈阳 110015rrrrrrrrn,沈阳 110015
论文部分内容阅读
本文研究了Ni-P化学镀A_(587)CL_1在人工海水溶液中的腐蚀疲劳寿命。结果表明,在不同疲劳载荷和不同频率下,镀层提高了试样的腐蚀疲劳寿命,在343MPa应力和0.3Hz频率时,提高到1.8倍左右,在147MPa应力时,提高到2.5倍(0.3Hz频率)和4.3倍(1.7Hz频率)。文章还根据疲劳试样及其断口形貌分析,讨论了镀层抑制疲劳过程的腐蚀行为和进一步提高腐蚀疲劳寿命的途径。
In this paper, the corrosion fatigue life of A-587 CL_1 Ni-P electroless plating in artificial seawater was studied. The results show that under different fatigue loads and different frequencies, the coating improves the corrosion fatigue life of the sample, which increases to about 1.8 times at 343MPa stress and 0.3Hz frequency and 2.5 times (0.3Hz frequency) at 147MPa stress ) And 4.3 times (1.7Hz frequency). Based on the analysis of the fatigue specimen and its fracture morphology, the article also discussed the corrosion behavior of the coating in the process of inhibiting the fatigue and the way to further improve the corrosion fatigue life.
其他文献
现阶段,随着中国教育教学改革工作的不断开展,如何将情景教学法融入高中生物学课堂教学已经成为广大生物学教育工作者共同关注的问题。在新课程标准改革的形势下,为了实现课
朱振林同志原是国有企业一名普通工人，改革开放的时代为他提供了发挥聪明才智的舞台。1984年他领导创建民办企业大武口铁合金厂，担任厂长，1990年实行一肩挑体制又担任党委书记。
男儿本自重横行天子非常赐颜色——唐·高适《燕歌行》 “峥嵘凌碧落,山势聚相灵”。相山,以她的巍峨挺拔,曲折绵延,为古都煤城淮北市相聚着人世间最
Boys copyrighted Hen
当前,专业模具厂的技术工人队伍青黄不接,不能适应对模具发展的要求,尤其是高级模具工缺额更大。由于缺少高级模具工,不少模具厂无力制造精密模具。 我厂经过充分准备,于198
目的:探讨氟伐他汀联合前列环素(PGI_2)对糖尿病肾病合并高脂血症动静脉内瘘血栓形成的防治作用。方法:将糖尿病肾病合并高脂血症并行动静脉内瘘成形术21例患者作为观察组采
本文介绍了用缓进给强力磨削工艺一次走刀磨削50mm深沟槽成型的工艺方法。研究了磨削深沟楷的尺寸精度和磨削表面质量。
This article describes the use of slow into the
周总理逝世已经20年了。抚今追昔,人们更加怀念他。 周恩来同志在道德风范上是大家公认的比较完美的典型。这一点不仅为我国广大人民群众所倾倒,也赢得了国外众多人士的由衷
应时代需求,初中的教学改天换地,从教学方式到教学模式甚至原本根深蒂固的老旧教学观念都有了极大的改变,学生们不再只是整日枯燥无味的学习,取而代之的则是趣味性十足的高效
A route was proposed to synthesize 3-benryl-glyceric acid (3-BGA) as an important intermediate for the synthesis ofa novel six-membered cyclic ester monomer -
最近10年来,脉管制冷机的研究工作取得了突飞猛进的发展,我国的有关研究工作处于国际先进水平,不少低温工作者在脉管制冷的理论与实验方面作出了突出的贡献,为世人所瞩目。其