【摘 要】
：
SnO2 thin films with good orientation are prepared on a glass substrate by radio frequence (RF) reactive sputtering. The phases of the thin films before and after annealing are analyzed by X-ray diffraction (XRD) spectroscopy, and the surface morphologies
【机 构】
：
AppliedScienceCollege,HarbinUniversityofScienceandTechnology,Harbin150080,China
【出 处】
：
ChineseOpticsLetters
论文部分内容阅读
SnO2 thin films with good orientation are prepared on a glass substrate by radio frequence (RF) reactive sputtering. The phases of the thin films before and after annealing are analyzed by X-ray diffraction (XRD) spectroscopy, and the surface morphologies of the thin films before and after annealing are analyzed by atomic force microscopy (AFM). The result shows that the crystalline quality of the films markedly improved, the grains grow a little, and the orientation is more consistent after annealing in the air at 400℃ for 60 min. After modular multi-grating spectrometer measurement, the average transmittance in the air is found to be 80%. By the scanning electron microscopy (SEM), the energy spectrum shows that the ratio of Sn and O is close to 1:2.
其他文献
利用固相反应法制备Zn0.9Co0.1O三维体材料,在不同的烧结温度下,应用单因素实验法对相同的配比成分样品进行处理,并对样品进行性能测试,寻找出最佳反应温度,为下一步沉积ZnO掺Co薄膜提供良好的靶材。分别对Zn0.9Co0.1O材料进行了X射线衍射(XRD)、拉曼(Raman)图谱和光致发光谱(PL)等进行了测试和分析。实验结果表明,烧结温度制约CO2 掺入ZnO晶格,并取代Zn2
我们证明，由于采用偏振的相干反斯托克斯喇曼光谱学，弱喇曼模的接收灵敏度得到极大的提高。共振非线性极化率的实部、虛部和绝对值谱能够分别予以测量。截面低至苯992厘米-1、模2×10-4倍的喇曼模用小于10千瓦峰值功率的激光器即可检测到。
研究了一个无损测量原子质心动量的精确可解模型,详细分析了无损测量的条件及无损测量的动力学过程。文中分析表明,绝热极限是实现此类模型无损测量的必要条件。最后针对此模型讨论了量子无损测量与表象之间的关系。
We have designed and fabricated zero-bias operational two-element symmetric-connected photodetector arrays (SC-PDAs). The designed SC-PDAs have higher saturation currents, larger RF power, and better frequency responses than the single photodetector (PD)
采用激光熔覆技术在GCr15钢基材上制备FeCrNiSi合金熔覆层，通过超景深显微镜、显微硬度计及摩擦磨损试验机，研究激光工艺参数对熔覆层显微组织、硬度及摩擦磨损性能变化的影响规律。结果表明：随着激光功率增大，熔覆层一次枝晶呈逐渐变大、变长的趋势，一次枝晶间距先增大后减小，二次枝晶间距逐渐减小；随着扫描速度加快，熔覆层一次枝晶呈先变大后减小的趋势，一次枝晶间距先增大后减小，二次枝晶间距先减小后增大。随着激光功率的降低或扫描速度的增加，熔覆层表面硬度提高，当激光功率为2400 W、扫描速度为7 mm/s时，
本文论述了35mm电影大孔径变焦距物镜的设计特点,提出了消象散中间固定组的结构。最后给出了具有中间固定组的新型变焦距物镜实例。它的焦距范围为25～85 mm,相对孔径为1/1.4,视场角为57°～18°。
研究了水、氯化镁、硫酸镁等无机盐水溶液及乙醇、乙腈等有机溶剂的光声温度效应。探讨了温度变化、液体分子结构弛豫和溶液特性改变对光声信号强度和峰形的影响。
设计了一种基于异质结构的低串扰3-LP模12芯光纤,纤芯采用异质无沟槽辅助的环形折射率分布,结构简单且能增大纤芯的有效模场面积。利用COMSOL软件分析了异质纤芯的芯间串扰、有效模场面积等性能,结果表明,异质纤芯LP01,LP11,LP21模的芯间串扰分别低于-0.78,-0.66,-0.4 dB/km,有效模场面积分别为150,166,200 μm 2。使用方点阵型纤芯排布方式,可实现包层直径约为213.8 μm、相对纤芯复用因子为26.9的低串扰3-LP模12芯光纤设计,为通信容量的升级扩容提供器件支
研究了强激光长程空气传输过程中主光束能量损耗与光束质量退化效应。使用1053 nm单波长、线偏振、脉宽3 ns平顶激光脉冲于空气环境中长距离传输，当入射光强与传输距离乘积大于13.7 TW/cm时，传输末端测得的光束光谱分布中出现了多种散射光频率成分，各散射光成分和1053 nm主激光间的频率差与氮气分子不同转动能级间跃迁频率一致，证明氮气分子的受激转动拉曼散射效应已建立。受激转动拉曼散射过程中，入射光束功率密度微弱变化所产生的散射光能量变化剧烈。入射光强与传输距离乘积大于17 TW/cm时，传输末端光束
High power laser diodes (LDs) with a lasing wavelength between 700 and 780 nm have great potential in various medical uses. Here, we report our recent efforts in developing an InGaAsP/AlGaInP-based commercial high power edge-emitting LD, which has 755 nm