As a decorative material,magnesium oxychloride cement was used as a photocatalyst supporter to purify the pollutants indoors.Due to excellent adsorption properties of activated carbon (AC),the photocatalytic composties,TiO2/AC,were prepared and introduced
【机 构】
：
State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
As a decorative material,magnesium oxychloride cement was used as a photocatalyst supporter to purify the pollutants indoors.Due to excellent adsorption properties of activated carbon (AC),the photocatalytic composties,TiO2/AC,were prepared and introduced into the porous magnesium oxychloride cement (PMOC) substrate to composite a sort of photocatalytic cementitious material (PCM).The optimal composite processes were assessed by gas chromatograph,using toluene as the target.By comparing the perspective of toluene purification and thorough decomposition,it can be found that the optimal mass ratio for TiO2/AC composites is 4/25,and the heat treatment to TiO2/AC sample at 350 ℃ can play the optimal synergetic role of adsorbents in photocatalytic process.The synergistic effect of TiO2,AC and magnesium oxychloride cement (MOC) was also evaluated by gas chromatograph.One-take molding process was adopted to introduce the TiO2/AC into PMOC substrate,and its optimal mass fraction was 4 wt％,while the appropriate density of substrate was 0.35 g/cm3.Toluene degradation showed that the prepared PCM can degrade pollutants efficiently.The appropriate treatment process of TiO2/AC,mass of TiO2/AC,substrate density,and stable pore structure should be coordinated to maximize the adsorption-photodegradation performance.The combination of photocatalytic materials,adsorbents,and building materials provided a new idea for the application of photocatalysis.
其他文献
The surface reconstructing of vermicular alpha-alumina exposed under electron-beam irradiation was investigated by a scanning electron microscope with 0.5 keV beam energy and by a transmittance electron microscope at room temperature and 90 K, respectivel
Fly ash and diatomite were mixed uniformly and ground within various time scale and fly ash/diatomite admixtures with variable particle sizes were obtained. Effects of particle size distributions of the admixtures on the mechanical properties and porosity
We prepared graphene oxide(GO) saturable absorber (SA) successfully through optical deposition method, which is a simple but effective approach to deposit various materials onto substrate under the effects of light, and investigated several factors that i
Barium ferrite micro/nano fibers were successfully prepared via the electrostatic spinning by using dimethyl formamide (DMF) as the solvent, and poly vinyl pyrrolidone (PVP) as the spinning auxiliaries. Effects of strontium substitution on the structure,
Single crystalline calcium chloroborate (Ca2B5O9Cl) whiskers with uniform diameter have been fabricated by a two-step process. The precursor was firstly prepared by the sedimentation reaction between CaCl2, H3BO3 and NaOH aqueous solutions, and then sinte
The damage process and corrosion ion distribution in concrete, which was exposed to 60 and 170 drying-immersion cycles of sulfate solution, were systematically investigated. The effects of plain concrete, plain concrete mixed with 4 and 8 kg/m3 modified P
At the initial rolling temperature of 250 to 400 ℃,AZ31B magnesium alloy sheets were hot rolled by four different rolling routes.Microstructures and mechanical properties of the hot-rolled magnesium alloy sheets were analyzed by optical microscope and ten
This paper aimed to improve the water-retention performance and basic physical properties of sulfoaluminate cement (SAC)-based planting cementitious material.The effect of natural zeolite on the performance of SAC-based planting material was investigated.
Significant efforts have been made in revealing the mechanism of thaumasite formation in concrete, which continues to be fraught with ambiguities and dissension. Chemical method was employed to synthesize pure C3S, C2S, C3A, ettringite, and thaumasite, an