【摘 要】
：
为了弄清钢流在浇注过程中受空气氧化的情况,进行了模型实验,得到的吸气公式为: V_g/V_1=2.433×10~_(-2)Fr~(0.4957)·We~(0.3122)·(h/D)~(0.3038) 还根据现场取样,分析浇
【机 构】
：
北京钢铁学院炼钢教研室,北京钢铁学院炼钢教研室
论文部分内容阅读
为了弄清钢流在浇注过程中受空气氧化的情况,进行了模型实验,得到的吸气公式为: V_g/V_1=2.433×10~_(-2)Fr~(0.4957)·We~(0.3122)·(h/D)~(0.3038) 还根据现场取样,分析浇注前后钢中氮含量以及氮氧之间关系,算出了钢液吸氧量,说明用上式估算钢水二次氧化程度是可行的。
In order to find out the situation of the steel flow being oxidized by air during the pouring process, the model experiment was carried out, the aspirating formula was obtained as follows: V_g / V_1 = 2.433 × 10 ~ (-2) Fr ~ (0.4957) · We ~ (0.3122 ) · (H / D) ~ (0.3038) It is also feasible to estimate the degree of secondary oxidation of the molten steel using the above formula, based on the site sampling, analysis of the relationship between the nitrogen content in the steel before and after casting and the nitrogen and oxygen, of.
其他文献
目的 观察外源性野生型p53对有p53基因突变的人肺癌细胞系生长的影响。方法 用PCR SSCP及DNA测序 ,选择p53突变的人肺巨细胞癌系 80 1 D。构建野生型p53表达质粒PZiP p53
癌肿的浸润和转移涉及一系列的复杂步骤，首先是细胞粘附系统的崩溃可致癌细胞分离，该系统包括整联蛋白、选择素、CD44和钙粘附蛋白分子放，其中钙粘附蛋白是一族透膜糖蛋白，发挥钙
病例 男,56岁。该患以上腹无痛性包块渐大六年为主诉住院。病人六年前在健康体检时经B超、CT检查发现腹部一包块约5.0cm,,以后包块逐渐增大,但无明显不适。入院检查,一般状
一、前言转炉炼钢的终渣,具有高温、高碱度、高氧化铁的内涵条件。因此,将出钢后剩余的终渣留在炉内,供下炉次冶炼之用,不仅可以加速成渣、节约石灰、降低铁耗;而且,还可以
滑膜肉瘤在软组织肉瘤中居第四位,约占所有软组织肉瘤的10％,其10年生存率仅11％～30％。 为检查滑膜肉瘸的MR特征及确定其非浸润性影像表现的出现频度,作者回顾性分析了1990年12月～1
影响壶腹部癌的预后因素很多。但神经周围微小浸润对壶腹部癌预后的影响目前还没有报道。因此作者对比研究了神经周围微小浸润和其它临床病理因素对壶腹部癌的预后影响。病人
本文研究所用的粉末为还原铁粉、电解铜粉(-200目)、石墨粉、羰基镍粉(-325目)和Pulverized(研成粉状)的磷铁合金(Fe-20％P)粉末。这些粉末以一定重量配比并加入1％的硬脂酸锌,
先天性阴蒂肿瘤【英】／ＬｅｖａｒｄＧ…／／ＪＵｒｏｌ．－１９９７，１５７（２）．－６４９先天性阴蒂肿瘤罕见。作者复习了有关儿科肿瘤的文献，新生儿这是第２例报告。病例报告：妊娠过程平稳出生的新生女婴，体检发现阴蒂有一个３５×１０ｍｍ园柱形灰色肿瘤，阴
对海绵钛粉、电解钛粉以及氢化脱氢钛粉进行了粉末热挤压的实验研究。观察了挤压材的组织结构并测定了材料的物理机械性能。结果表明,挤压材中多数孔隙由粉末中的夹杂物造成
据英刊《金属通报》报道。法国一家名叫爱西丽丝·蒙特里尔的小钢联(SAM)最近建造了一个可从炼钢厂烟道灰中提取锌和铅的新厂,该装置现已投入使用,它将处理该厂和另一家姐妹