SiCp/Gr/2024Al metal matrix composites were processed by squeeze casting technology. The microstructure of composites was observed by SEM and TEM, and the effects of graphite particulates and SiC particulates on the damping behaviors of composites were also investigated. The results show that the microstructure of composites was dense and homogeneous, without any interfacial reactivity among reinforcement/matrix interfaces. Compared with the damping capacity of 2024Al, the damping capacity of composites was enhanced significantly by addition of SiC or graphite particulates. The main damping mechanisms of SiCp/Al composites were ascribed to the dislocation damping, and those of SiCp/Gr/2024Al were attributed to the intrinsic damping and interface damping.