采用废旧PET(polyethylene terephthalate)作为胶凝材料制备PET-黏土砖粉砂浆。研究了PET-砖粉砂浆的吸水率、抗硫酸盐侵蚀性、抗氯离子渗透性,并通过SEM观察其微观形貌。研
【机 构】
：
山东大学土建与水利学院,山东省实验中学,
论文部分内容阅读
采用废旧PET(polyethylene terephthalate)作为胶凝材料制备PET-黏土砖粉砂浆。研究了PET-砖粉砂浆的吸水率、抗硫酸盐侵蚀性、抗氯离子渗透性,并通过SEM观察其微观形貌。研究结果表明,试件的7 d吸水率为0.9%;20个循环后浸泡在硫酸盐溶液与清水中的试件抗压强度仅相差1.83%;PET-砖粉砂浆的氯离子电通量为48 C。因此PET-砖粉砂浆具有很好的耐久性。SEM结果表明材料内部较好的密实度,呈现极少的孔隙。
Waste PET (polyethylene terephthalate) as a cementitious material to prepare PET-clay brick mortar. The water absorption, sulfate attack resistance and chloride ion resistance of PET-brick mortar were studied. The microstructure of PET-brick mortar was observed by SEM. The results showed that the water absorbency of the specimens was 0.9% after 7 days, and the compressive strength of the specimens immersed in the sulfate solution and water after 20 cycles was only 1.83%. The chloride flux of PET-brick mortar was 48 C. Therefore, PET-brick powder mortar has good durability. The SEM results show better internal compaction of the material with very few pores.
其他文献
俗话说得好,“桂林山水甲天下”。桂林山清水秀,风景如画,美丽无限。而我却独爱那夜色中艳丽迷人的两江四湖!那天晚上九点多,我们迫不及待地上了船。刚刚坐定,船就开动了。
目的综合评价足月低出生体重儿(low birth weight infant,LBWI)的影响因素。方法采用病例对照研究方法,对66例低出生体重儿和1 743例正常出生体重儿的母亲进行回顾性分析。结
本刊讯（通讯员 郑军）8月16日，由河北省粘接与涂料协会、香港高路集团（中国）有限公司发起，保定光普化工研究所、上海光普化工有限公司主办的“直隶论剑—2015水性胶粘剂高峰论坛暨保定光普化工研究所成立10周年庆典”，在河北保定顺利召开。天津大学、河北大学、河北科技大学等高校的知名专家学者，香港高路集团全体成员、河北省粘接与涂料协会相关会员单位、浙江顶立、西安汉港、湖州华通、上海协成永固、江西宜春正
邮发代号24–42,24–138全国各地邮局均可订阅欢迎广大读者到当地邮政局(所)订阅2016年《工程塑料应用》、《化学分析计量》杂志,订阅杂志及合订本光盘及过期刊物的读者可直
The aim of this study was to explore the effects of parenteral supplementation with ω-3 fish oil emulsion (Omegaven) on systemic inflammatory response syndro
Most current lattice Boltzmann(LBM) models suffer from the deficiency that their parameters have to be obtained by fitting experimental results.In this paper,we
A ternary self-condensing vinyl polymerization(SCVP) system consisting of monomers, inimers and core initiators is studied by the principle of statistical mecha
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
摘 要： 以英语独特的魅力，激发学生的兴趣，引领他们体会学习的快乐，不断累积成就感，培养良好的心理优势，从而学习英语也就事半功倍。心理优势表现为师生在积极互动中呈现出的那种力求成功的心向，这符合当前实施素质教育的主流。文章就如何培养中学生学英语的心理优势谈几点体会。 关键词： 培养 学习英语 心理优势 不同字母的组合，不一样的发音，不一样的意思，独特的英语魅力，一开始就会吸引学生，令他们欣
从项目的初步设计、详细设计两个阶段根据某炼油项目的中间原料罐区上下游各相关装置生产运行的不同工况,进行了转输泵不同配置方案的设计。
From the preliminary design a