玻璃纤维缠绕制品,在固化过程中,由于工件温度滞后于固化炉指示温度、工件外层与内层的温度不同等原因,有时发现按一般固化制度进行固化,其结果工件没有完全固化,或外层已固化而内层固化不完全,未达到预期的固化程度。因对缠绕制品在固化炉内的实际固化情况不清楚,影响制品的性能,为此需解决在实际固化过程中,确定特定的固化制度,以确保工件完全固化。 在实际固化过程中,我们用介电法(介质
Glass fiber winding products, in the curing process, due to the workpiece temperature lag behind the curing oven temperature, the temperature difference between the outer layer and the inner layer of the workpiece and other reasons, sometimes found cured according to the general curing system, as a result of the workpiece is not fully cured, or outside The layer has cured and the inner layer is not fully cured, failing to achieve the desired degree of cure. Due to the actual curing of the wound product in the curing oven is not clear, affecting the performance of the product, to be solved in the actual curing process, to determine the specific curing system to ensure the workpiece is fully cured. In the actual curing process, we use the dielectric method (medium