【摘 要】
：
The Mg-8Sn-4Zn-2Al (TZA842,in wt％) alloys with different initial microstructure (as-cast-AC and homogenization treatment-HT) subjected to hot extrusion.Also,the strengthening responses to AC and HT for the extruded TZA842 alloys were reported.The results
【机 构】
：
School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China
论文部分内容阅读
The Mg-8Sn-4Zn-2Al (TZA842,in wt％) alloys with different initial microstructure (as-cast-AC and homogenization treatment-HT) subjected to hot extrusion.Also,the strengthening responses to AC and HT for the extruded TZA842 alloys were reported.The results revealed that the alloy subjected to HT shows finer grain size,more homogenous microstructure and weaker basal texture than those of counterpart subjected to AC.In addition,compared with TZA842-AC alloy,precipitates were finer and uniformly dispersed in TZA842-HT owing to the utilization of HT.Moreover,the TZA842-HT alloy showed higher yield strength of 200 MPa,ultimate tensile strength of 290 MPa and elongation (EL) of 17.9％ than those of TZA842-AC,which was mainly attributed to the combined effects of grain boundary strengthening,precipitation strengthening,solid solution strengthening and weak texture.Strengthening mechanism for both alloys was discussed in detail.
其他文献
Classical powder metallurgy followed by either hot isostatic pressing (HIPing) or repressing-annealing process was used to produce Cu-graphene nanoplatelets (GNPs) nanocomposites in this work.A wet mixing method was used to disperse the graphene within th
In this work, the shear model of metal melt flowing on vibration surface is established, and coupling effects of vibration and shear on the distribution of shear stress in melt and melt solidification microstructure are analyzed. Calculation results show
The morphological evolution of Fe-rich phases in the AlSi9Cu3Mg0. 19(Fe) alloy has been investigated with various contents of Fe, Mn, and Cr. The results show that coarse Chinese script Fe-rich phases appear in the alloy with 0. 6 wt％ Fe combined with tra
Magnesium matrix composites reinforced with AlN particles were fabricated by the powder metallurgy technique. Different mixing methods were used in this study to control the distribution of AlN particles. The microstructure, thermal diffusivity and therma
A facile polyol-assisted pyro-synthesis method was used to synthesize Co3O4 nanoparticles embedded into carbon matrix without using any conventional carbon source.The surface analysis by scanning electron microscopy showed that the Co3O4 nanoparticles (～2
A polymethyltrimethoxysilane (PMTMS)/hydroxyapatite (HA) hybrid coating was successfully fabricated on a magnesium alloy by hydrothermal treatment and immersion method.The microstructure and composition of the coating were characterized by using X-ray dif
The growth behavior of Al3Ni intermetallic compounds (IMCs) during the directional solidification of Al-10 wt％ Ni alloy was investigated by synchrotron radiography. Two main growth patterns of primary Al3Ni phase, I-like and V-like, appeared during solidi
Sand-cast Mg-9Gd-4Y-0.5Zr (wt％) alloy was solution-treated at 500-565 ℃ in the time range of 0.5-30 h in air or vacuum to investigate its microstructure evolution and mechanical properties.The results showed that solution treatment temperature had a signi
The different solution and migration behaviors of tetrahedral and octahedral interstitial helium in bcc iron have been investigated by using first principles calculations.We showed that the tetrahedral site has less charge transfer and less redistribution