【摘 要】
:
Open-celled porous (TiB2-Al2O3)/NiAl composites were successfully fabricated by using spherical carbamide as space holders via self-propagating high-temperature synthesis (SHS).Effects of 10Al-3B2O3-3TiO2 contents (0-20 wt%) on the pore structures and the
【机 构】
:
School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao
论文部分内容阅读
Open-celled porous (TiB2-Al2O3)/NiAl composites were successfully fabricated by using spherical carbamide as space holders via self-propagating high-temperature synthesis (SHS).Effects of 10Al-3B2O3-3TiO2 contents (0-20 wt%) on the pore structures and the quasi-static compressive behaviors of the resultant materials were investigated.The porous (TiB2-Al2O3)/NiAl composites exhibit composite pore structure consisting of homogeneously distributed and interconnected millimeter pores and micropores.The millimeter pores virtually inherit the shape and size of carbamide particles,while the pore size of micropores increases with increasing the 10Al-3B2O3-3TiO2 content.Depending on the volume fraction of the carbamide,the porosity of the porous materials can be easily controlled in a range of 55%-85%.When the porosity is about 72%,the compressive strengths of porous NiAl and porous (TiB2-Al2O3)/NiAl composite with 15% 10Al-3B2O3-3TiO2 in green compact are 19 and 32 MPa,and the corresponding strains are 2.9% and 5.7%,respectively.Furthermore,the quasi-static compressive behavior of porous (TiB2-Al2O3)/NiAI composites can be estimated by Gibson-Ashby model.
其他文献
The variant selection of martensites (ε-M and α\'-M) and ε-M reversion in dynamic tensile high-manganese TRIP steel were investigated.α\'-M variant pairs with a zigzag morphology frequently formed,and the pairs of neighboring α\'-M variants were exa
The influence of asymmetric reduction rolling (ARR) on the microstructure,texture and mechanical properties of AZ91 was investigated.The microstructural characteristics of the AZ91 sheet processed by symmetric rolling (SR) were the twins,intersection of t
Young\'s modulus is a critical parameter for designing lightweight structure,but Al and its alloys only demonstrate a limited value of 70-72 GPa.The introduction of carbon nanotubes (CNTs) is an effective way to make Al and its alloys stiffer.However,li
The influence of long-term solution treatment for various intervals on the microstructure, mechanical properties, and corrosion resistance of the as-cast Mg-5Zn-1. 5Y alloy was investigated. Variation of secondary phases was studied during solution treatm
Corrosion resistance behavior of Co-containing maraging stainless steels was investigated.Neutral salt spray and polarization test showed that maraging stainless steel with high Co content showed poor corrosion behavior.Microstructure observation proved t
Pulsed external field,including electric,magnetic,ultrasonic and laser,as an instantaneous high energy input method with high efficiency and low energy consumption,have long been known to can modify the microstructure and properties of materials.This incl
The (La4MgNi17.5Mn1.5) alloys at different melt-spun speeds were prepared by using a vacuum melt-spun furnace,and the phase structure and electrochemical properties of alloys were studied.X-ray diffraction analysis results show that melt-spun La4MgNi17.5M
The Al-2.5C master alloy is prepared to investigate the effect of the Al4C3 particle size distribution on the refining efficiency of the AZ31 alloy.The results indicate that the Al4C3 particles are potent nucleation substrates for primary α-Mg grains.With
The present work focuses on the structural stability upon hydrogenation of three typical La-Mg-Ni-based alloys: La2-MgNi9, La3MgNi14 and La4MgNi19. Structural changes during gaseous and electrochemical cycles were characterized, and the influence of the s