Phase Structure and Electrochemical Properties of Melt-Spun La4MgNi17.5Mn1.5 Hydrogen Storage Alloys

来源 :金属学报(英文版) | 被引量 : 0次 | 上传用户:flywhc
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The (La4MgNi17.5Mn1.5) alloys at different melt-spun speeds were prepared by using a vacuum melt-spun furnace,and the phase structure and electrochemical properties of alloys were studied.X-ray diffraction analysis results show that melt-spun La4MgNi17.5Mn1.5 alloys are composed of CeCus-type,Pr5Co19-type and CeNi2-type phase.As the melt-spun speed increased,the phase abundance of CeCu5-type increased,but that of Pr5Co19-type decreased.Scanning electron microscopy-energy-dispersive spectroscopy analysis results show that melt-spun treatment can refine grain and make the alloys homogenization.Electrochemical tests show that all alloys have good activation performance within four cycles.With the increase in melt-spun speed,the cycle stability (S) of the alloys was improved obviously.After 100 cycles,the retention rate (S100) of the alloy increased from 54.82% (as-cast) to 82.29% (25 m/s).Nevertheless,the maximum discharge capacity (Cmax) and high-rate dischargeability gradually decreased.
其他文献
Mg-3Al-1Zn alloy sheets have been deformed by continuous bending (CB) to investigate the effects of processing parameters (bending angle and repetitive passes) on the texture and formability.The samples exhibited a bimodal microstructure with abnormal gro
The microstructure,texture,residual stress,and tensile properties of Mg-6Zn-2Y-1La-0.5Zr (wt%) magnesium alloy were investigated before and after extrusion process,which performed at 300 ℃ and 400 ℃.The microstructural characterizations indicated that the
A modified strain-induced melt activation (SIMA) process consisting of homogenization,equal-channel angular pressing (ECAP) and subsequent heating to the semisolid temperatures was introduced to prepare the 7075 aluminum alloy with superior thixotropic be
The variant selection of martensites (ε-M and α\'-M) and ε-M reversion in dynamic tensile high-manganese TRIP steel were investigated.α\'-M variant pairs with a zigzag morphology frequently formed,and the pairs of neighboring α\'-M variants were exa
The influence of asymmetric reduction rolling (ARR) on the microstructure,texture and mechanical properties of AZ91 was investigated.The microstructural characteristics of the AZ91 sheet processed by symmetric rolling (SR) were the twins,intersection of t
Young\'s modulus is a critical parameter for designing lightweight structure,but Al and its alloys only demonstrate a limited value of 70-72 GPa.The introduction of carbon nanotubes (CNTs) is an effective way to make Al and its alloys stiffer.However,li
The influence of long-term solution treatment for various intervals on the microstructure, mechanical properties, and corrosion resistance of the as-cast Mg-5Zn-1. 5Y alloy was investigated. Variation of secondary phases was studied during solution treatm
Corrosion resistance behavior of Co-containing maraging stainless steels was investigated.Neutral salt spray and polarization test showed that maraging stainless steel with high Co content showed poor corrosion behavior.Microstructure observation proved t
Pulsed external field,including electric,magnetic,ultrasonic and laser,as an instantaneous high energy input method with high efficiency and low energy consumption,have long been known to can modify the microstructure and properties of materials.This incl