Ni-W alloys and their composite deposits are electroplated on the metals when an appropriate complex agent is selected on the base of the theories of electrochemistry and complex chemistry, and the principle of induced codeposition. Effects of the bath composition, pH value, temperature and current density on the electrode position of Ni-W alloys and their composite deposits have been investigated, and the effect of heat treatment temperature on the hardness, structure and cohesive force of the amorphous Ni-W alloys and their composite deposits are also discussed. Results showed that the alloys containing more than 44 wt pct W content and the composite deposits containing 7.8 wt pct SiC content could be obtained by making use of the appropriate bath composition and plating conditions. Alloys and their composite deposits with over 44 wt pct W content show amorphous structure. The hardness of amorphous Ni-W alloys and their composite deposits increases obviously when heated, and can reach to 1350 HV and 1520 HV respectively for 46 wt pct W content. The cohesion on Cu, carbon steel and stainless steel is very good.
Ni-W alloys and their composite deposits are electroplated on the metals when an appropriate complex agent is selected on the base of the theories of electrochemistry and complex chemistry, and the principle of induced codeposition. Effects of the bath composition, pH value, temperature and current density on the electrode position of Ni-W alloys and their composite deposits have been investigated, and the effect of heat treatment temperature on the hardness, structure and cohesive force of the amorphous Ni-W alloys and their composite deposits are also discussed. showed that the alloys containing more than 44 wt pct W content and the composite deposits containing 7.8 wt pct SiC content could be obtained by making use of the appropriate bath composition and plating conditions. Alloys and their composite deposits with over 44 wt pct W content show amorphous structure. The hardness of amorphous Ni-W alloys and their composite deposits increased obviously when heated, and can reac h to 1350 HV and 1520 HV respectively for 46 wt pct W content. The cohesion on Cu, carbon steel and stainless steel is very good.