A series of hyperbranched poly (amine-ester)polyols were synthesized by the polycondensation of N, Ndiethylol- 3- amine-methylpropionate (prepared by Michael addition reaction of methyl acrylate with diethanolamine) as an AB2- type monomer with trimethylol propane as the core moiety, proceeding in one-step procedure in the melt with ptoluenesulfonic acid as catalyst. The obtained monomer and polymers were characterized by FTIR and 1H-NMR spectroscopy. The solubility and surface activity in aqueous solution of the polymers were also examined. The gas permeability, water vapor permeability, and moisture absorption of microfiber synthetic leather treated by hyperbranched polymer were studied. The optimum conditions were that the dosage of dye and hyperbranched polymer was 5% and 10%, respectively. The water vapor permeability and moisture absorption of microfiber synthetic leather reached to 0. 525 4 mg/( 10 cm2 · 24 h) and 0.046 7 mg/(10 cm2 · 24h). Compared with blank samples, they increased by 15% and 35%, respectively.However, the dosage of hyperbranched polymer has little influence on gas permeability of microfiber synthetic leather.SEM results show that the fiber of microfiber synthetic ieather treated by hyperbranched polymer is incompact.