Four CrAlN coatings with various Al content were prepared by arc ion plating technology under different target currents.The effect of the Al content on the microstructure,chemical compositions,element chemical bonding states and mechanical properties of the CrAlN coatings was analyzed.X-ray diffraction results show that the primary phase of the CrAlN coating is fcc-(Al,Cr)N when the Al content is about 44.02 at.％.However,when the Al content increases to about 53.34 at.％,hcp-AlN phase emerges in the coating.And the hcp-AlN phase becomes the main phase in the CrAlN coating with Al content of about 69.55 at.％.Cross-sectional images show that all the four coatings possess dense structures and the deposition rate of Al atom is higher than that of Cr atom.The hardness of the CrAlN coating with Al content about 44.02 at.％ is the largest (3149.72 HV) due to the solid solution hardening effect of the Al element.When the hcp-AlN phase is generated in the CrAlN coating,the hardness declines.The tribological experiment shows that the wear resistance of the CrAlN coating decreases gradually with increasing Al content when sliding against 100Cr6 steel ball.