Hydrothermal synthesis and luminescent properties of LixEuxSr1-2xMoO4red phosphor

来源 :稀土学报(英文版) | 被引量 : 0次 | 上传用户:liuyongqiang615
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
LixEuxSr1-2xMoO4 red phosphors were synthesized via a facile hydrothermal method with various reaction time and ion contents of Eu3+ and Li+.As-synthesized samples were characterized by X-ray diffraction (XRD),thermogravimetry (TG),field emission scanning electron microscopy (FE-SEM) and fluorescence spectrophotometry.The XRD results revealed the formation of scheelite-like phosphor structures.The excitation spectra indicated the presence of two main excitation peaks located at 396 and 466 nm,suggesting that this phosphor could be excited well by GaN-based near-UV and blue LED chips.The emission spectra under 466 nm excitation exhibited dominant peaks centered at 614 nm.The influence of reaction time and ions content on the luminescent properties of LixEuxSr1-2xMoO4 was also investigated.The results indicated that reaction time of 48 h was appropriate,and the maximum luminescent intensity was obtained when a molar ratio of 40% ions content was employed.
其他文献
Binary Ce-Zr (CZ),Pr-Zr (PZ) and ternary Ce-Zr-Pr (CZP) mixed oxides were prepared by an ammonia-aided co-precipitation method,and were aged in a steam/air flow
Er3+ and Li+ codoped Y3Al5O12 (YAG) powders were prepared for a systematic investigation of their upconversion emissions.X-ray diffraction (XRD),upconversion em
we developed a new silicate-based full-color phosphor Ba3Lu2(SiO4)3:Et2+ through solid state reaction.The host crystal structure was isostructural with Ca3Y2(Si
通过湿法球磨制备CoFe2O4-BaTiO3颗粒复合材料,研究材料成分和调制频率与电磁效应的关系.结果表明:电磁效应系数随着调制频率由400 Hz增加到1 000 Hz而增加.由于CoFe2O4的电
Nanocrystalline cubic Y2O3:Eu were prepared by combustion reaction.The crystal structure and morphology were analyzed by means of X-ray diffraction (XRD) and tr
Uniform YF3 nanorods composed ofnanoparticles were successfully prepared via a facile solvothermal method with ethanol as solvent and tetrabutyl ammonium fluori
The water repellence and mechanical properties of the gelatin/Ce(Ⅲ) fiber (GCe fiber) were improved by heat treatment,which was an easy and non-toxic method.Th
Monodispersed and water-soluble TbF3 nanoparticles were synthesized at a relatively low temperature in aqueous solution using citric acid as an additive,and cha
(Ba0.5Sr0.5)1-xPrxCo0.8Fe0.2O3-δ (BSPCFx;x=0.00-0.30) oxides were synthesized by a sol-gel thermolysis process using combination of PVA and urea,and were also
The influence of rare earths (RE) on solidification behavior of a high speed steel for roll was investigated by using differential scanning calorimetry (DSC) in