【摘 要】
:
对硝酸级(NAG)310L不锈钢焊接接头在含氧化性离子的沸腾硝酸中进行浸泡实验及金相分析。研究表明,在不同Cr~(6+)含量的沸腾40%HNO_3中,材料的腐蚀程度主要受Cr~(6+)含量的影
【机 构】
:
中国钢研科技集团公司,北京科技大学材料学院,
论文部分内容阅读
对硝酸级(NAG)310L不锈钢焊接接头在含氧化性离子的沸腾硝酸中进行浸泡实验及金相分析。研究表明,在不同Cr~(6+)含量的沸腾40%HNO_3中,材料的腐蚀程度主要受Cr~(6+)含量的影响。随Cr~(6+)含量的增加,母材和焊缝均出现不同程度腐蚀,但焊缝较母材腐蚀严重。Cr~(6+)含量是促进焊缝过钝化腐蚀和晶间腐蚀的主要因素。
The soaking experiment and metallographic analysis of 310N stainless steel welded joints of nitric acid grade (NAG) in oxidizing nitric acid with oxidizing ions were carried out. The results show that the corrosion degree of the material is mainly affected by the content of Cr 6+ in boiling 40% HNO 3 with different content of Cr 6+. With the increase of Cr 6+ content, the base metal and weld all showed different degrees of corrosion, but the weld was more corroded than the parent metal. The content of Cr 6+ is the main factor to promote the passivation corrosion and intergranular corrosion of weld.
其他文献
用电化学阻抗谱(EIS)、电化学噪声(EN)及扫描电子显微镜(SEM)研究磷酸锌对磷酸锌/环氧涂层的保护作用及其保护尺寸的变化规律。研究表明,磷酸锌使划痕处的腐蚀产物变得致密,
陈水根,男,1956年12月14日出生,江西省丰城市人,汉族,大专文化,生前曾任南昌市青云谱区法院民事审判一庭副庭长,主任科员,一级法官。从事民事审判工作近二十年来,他凭着对法
本次连片处理涉及的SD 工区由SD1、SD2、SD3 三个工区组成。由于各个工区施工年度及采集参数不同,提供的野外静校正量不齐全。除常规静校正问题外,本工区还存在区块之间连片时
共偏移距道集在复杂介质中因地震波传播的多路径而存在地下反射位置不准确的问题。共反射角道集(CIG)由于克服了上述缺陷而成为复杂区精确成像、AVA 分析及保幅偏移成像研究的
采用溶胶-凝胶法在304不锈钢表面制备了铈掺杂TiO_2薄膜,并采用半连续培养方式在海水中培养硫酸盐还原菌(SRB)。通过形貌观察及电化学方法研究浸泡于菌液中的空白304不锈钢及
采用扫描电镜(SEM/EDX)、失重法等研究了7A04铝合金在两种模拟SO2气氛条件下的腐蚀行为和规律,以及与江津大气暴晒试验结果的相关性。结果表明,随试验时间的延长,铝合金腐蚀
新疆东部石炭系火山岩发育,剩余重力揭示东疆地区石炭系存在七个残留凹陷中,勘探程度很低,目前,已在ML 凹陷石炭系火山岩中发现多个油田。由于石炭系火山岩自身的特殊性和复杂的
用电化学方法和衰减全反射傅立叶红外(ATR-FTIR)技术研究了月桂酸对N80钢在不同pH值(4.9、6.9和7.4)的CO_2饱和盐水溶液中的缓蚀行为和机理。试验结果表明月桂酸在低pH值下对
用开路电位法、极化曲线法和电化学阻抗技术研究硫酸盐还原菌(SRB)对铜镍锡合金腐蚀行为的影响。用扫描电镜(SEM)和能谱分析(EDS)观察铜镍锡合金的腐蚀形貌。结果表明,SRB的
在模拟加氢反应器工况条件下,研究氢对加氢反应器器壁材料2(1/4)Cr-1Mo钢的力学性能的影响。采用低周疲劳实验计算原始状态和渗氢试样的裂纹扩展速率da/dN及门槛值△J_(th);