3D reticulated ceramics (3DRCs) with the composition containing SrFe12O19-SiC-TiO2 were prepared by a replication process with polyurethane sponges as the template in ceramic slurry. The electrical conductivity, dielectric and magnetic parameters of 3D reticulated ceramics (3DRCs) were measured with changes in cell size of the sponges, contents in the slurry and sintering temperature in this paper. Discussions about the influential factors of those parameters were focused on their electrical conductivity. The experimental results indicated that the electrical conductivity of 3DRCs raised with the increase of cell size, SiC/SrO 6Fe2O3 with weight ratio and sintering temperature. X-ray diffractions and SEM were used to investigate the relationship between electrical conductivity and sintering temperature. Deoxidizing reactions of SrO 6Fe2O3 caused the increasing electrical conductivity. The real part of permittivity (ε’) and imaginary part of permeability (μ“) raised with the increase of electrical cond
The electrical conductivity, dielectric and magnetic parameters of 3D reticulated ceramics (3DRCs) were measured with changes in cell size of the sponges, contents in the slurry and sintering temperature in this paper. Discussions about the influential factors of those parameters were focused on their electrical conductivity. The experimental results that the electrical conductivity of 3DRCs raised with the increase of cell size , X-ray diffractions and SEM were used to investigate the relationship between electrical conductivity and sintering temperature. Deoxidizing reactions of SrO 6Fe2O3 caused the increasing electrical conductivity. The real part of permittivity (ε ’ ) and imaginary part of permeability (μ ”) raised with the increase of electrical cond