The structure of micelles formed by two poly(oxyethylene)/poly(oxybutylene) block copolymers, E 76B 38 and E 155B 76, in n-hexane at 50 ℃ was studied by synchrotron Small Angle X-ray Scattering(SAXS) and Wide Angle X-ray Scattering(WAXS). Spherical micelle with a crystalline core was observed for E 155B 76. E 76B 38 also formed spherical micelles, but the core was amorphous. The radius of the core(R), the length of the amorphous chain in the shell(L) and the number of association(N) were obtained by fitting the SAXS data with the model of a spherical core attached with Gaussian chains. The result showed that the E block exhibited multiple folds. The B block tended to be more coiled and the area occupied by per chain was larger in the micelles of E 155B 76, which are favorable to the formation of spherical micelles.
The structure of micelles formed by two poly (oxyethylene) / poly (oxybutylene) block copolymers, E 76B 38 and E 155B 76, in n-hexane was studied by synchrotron Small Angle X-ray Scattering (SAXS) The radius of the core (R), the length of the amorphous chain (WAXS). Spherical micelle with a crystalline core was observed for E 155B 76. E 76B 38 also formed spherical micelles, but the core was amorphous. in the shell (L) and the number of association (N) were obtained by fitting the SAXS data with the model of a spherical core attached with Gaussian chains. The result showed that the E block rendered multiple folds. The B block tended to be more coiled and the area occupied by per chain was larger in the micelles of E 155B 76, which are favorable to the formation of spherical micelles.