摘要：随着我国建筑工程技术的发展，大型的城市标志和高层的建筑设施越来越多，所以，在建筑工程中应用和施工大体积混凝土是势在必行的事情。和其他的混凝土施工方法不同，大体积混凝土施工需要更加严格的技术和流程。当前有许多的工程项目都开始采用大体积混凝土的施工方式，但是，我们经常可以发现，在大体积混凝土的浇筑过程中很 容易形成细小的裂缝。对混凝土而言，存在裂缝就是存在着质量问题，所以要进行必要的预防、治理和控制。
关键字：建筑工程；匹配；水化热；温度控制措施；大体积混凝土；施工技术；浇筑
Abstract:With the development of construction technology in our country, big city logo and high-rise building facilities is more and more, therefore, is applied in the architectural engineering and construction of large volume concrete is to be imperative. Unlike other concrete construction method, the construction of large volume concrete need to be more strict technical and process. The construction project, many are beginning to use the large volume concrete. However, we often can discover, cracks in the construction process of mass concrete is easy to the formation of fine. For the concrete cracks, there is the existence of quality problems, so to prevent, manage and control the necessary.
Keywords: building engineering; matching; hydration heat; temperature control; mass concrete; construction technology; concrete
中图分类号：TV544+.91文献标识码：A文章编号：
1.在工程结构中大体积混凝土是整个建筑的基础，对于大型建筑有著很重要的作用，但是在混凝土的配置过程中如果不能合理的适当的处理混凝土水化热所引起的温度作用和混凝土自身的收缩膨胀等变形而产生的较大的温度应力，设计施工就可能会产生极具危害性的裂缝。
1.1在我国过去经常采取在建筑的过程中设置伸缩缝或者后浇带的方法来解决大体积混凝土的出现裂缝的现象。但是，随着建筑的发展，建筑工期的要求，以及由于建筑自身结构的整体性、功能性的客观要求等，现在很多企业对于这类建筑要求无缝施工。所以，我们不得研究和探讨如何在施工中不设置伸缩缝和后浇带也能够满足大体积混凝土建筑的设计和工程质量的要求。
1.2在国内对于大体积混凝土的定义中，机考虑了混凝土的几何尺寸，同时也考虑了由于在配置大体积混凝土的过程中因为水化热而引起的体积变化和裂缝问题。
1.3对于大体积混凝土目前国际上也没有统一的定义，在美国混凝土学会认为大体积混凝土是“现场浇筑的混凝土，尽最大到需要采取措施降低水化热和水化热引起的体积变化。以最大限度地减少混凝土的开裂。”这说明了在大体积混凝土的混凝土的建筑过程中由于水化热而引起的体积变化和开裂问题是其中最主要的和最需要想办法解决的技术问题。
2.现代的建筑中，时常会涉及到大体积的混凝土的施工，例如高层楼房的基础、大型设备基础或者水利大坝等等。大体积混凝土施工都有哪些特点呢。
2.1大体积混凝土的最主要的特点就是体积大，一般实体最小尺寸大于或等于1m，同时水化热引起混凝土内部的最高温度与外界气温之差预计超过25℃的混凝土。
2.2表面系数比较小，水泥水化热释放比较集中，内部温升比较快，所以大体积混凝土内外温差较大。
2.3大体积混凝土结构的几何尺寸较大,且必须采用技术措施以避免水泥水化热及体积变化引起裂缝的结构，其结构尺寸已经大到必须采取相应的技术措施,妥善处理温度差值、合理解决温度应力、并按裂缝开展进行处理及控制的混凝土施工技术。
3.首先就是要科学合理的做到大体积混凝土的配合比。在大体积混凝土的施工过程中，水凝水化时会产生一定温度的水化热，从而引起水泥温度的上升，但是温度上升的部位和程度都是不一样的，从而引起混凝土不同部位的温差可能会过大，温度应力如果超过了混凝土的抗拉强度就会导致混泥土随后出现细小的裂缝。
3.1刚才我们已经说过，大体积混凝土出现裂缝的一个主要原因就是水泥水化的过程中会产生水化热，而水化热引起的温差会导致混凝土开裂，所以在保证混凝土的质量的前提下降低单位水泥的比例，降低水泥用量是控制水化热所产生的温度的一项很重要的措施。
3.2也可以在配置水泥的过程中加入适量的粉煤灰，粉煤灰会有效的延缓混凝土配置在中所产生的水化热的释放时间，这样一来对于大体积的混凝土的温度的控制是很有利的。同时，在大体积混凝土中掺入粉煤灰还可以增强混凝土的后期强度，有效的保证提高混凝土强度，可以取得一举两得的效果。
3.3NF型缓凝高效减水剂是对大体积混凝土进行温控的最有力的外加剂之一。使用缓凝型外加剂可以有效的控制和延缓配置水泥过程中的所产生的水化热的释放时间，可以有效地降低混凝土在某一瞬间温度会和高很高，而是水化热的释放就会变得比较的平缓，这样就可以有效的避免由于水化热而导致的温差过大的现象。
3.4大体积混凝土开裂的原因除了是有于配置混凝土的过程中水化热所长生的温度造成的之外，还有一个重要的原因是由于所选用的水泥的种类和质量，所以，在建筑工程的过程中国，一定要选用优质的水泥。
3.5也可以通过改善混凝土的体积的稳定性来提高混凝土的抗裂性能，例如在配置混凝土的过程中掺入一定量的粗骨料就可以有效的改善混凝土的抗裂能力；也可以在保证混凝土的强度和施工方便的前提之下降低混凝土的含砂率，从而减少出现裂缝的可能性。
3.6外界的气候变化也是重要的影响因素之一。大体积混凝土在施工的过程中，外界的气温的变化对于混凝土的影响是很大很明显的。外界气温升高和气温的降低，都会带动大体积的混凝土的温度的升高和降低。特别是外界气温的骤降，就会增加整体的大体积的混凝土的外部和内部的温度梯度，这对于大体积混凝土的凝结和长久使用是很不利的一件事情。
4.建筑是由各种各样的建筑材料来完成的，所以选用合适的建筑材料是很重要的，只有选用正确的建筑材料，才能更好地解决建筑工程中所遇到的各种的问题。对于大体积混凝土施工技术而言，选择合适的建筑材料和正确的施工技术同样的重要。
4.1大体积混凝土首要要考虑的就是水泥的选用了。水泥之所以会造成温差，主要的原因是由于水泥在配置的过程中由于水热化而产生的。因此，减小温差的一个重要的办法就是尽量的避免混凝土的水热化现象，为了避免水热化现象的出现，可以选用具有早期水热化低的水泥材料。水泥出现水热化的原因是由于矿物成分和细度的函数，所以降低水泥的水热化现象可以可以选择何有一定量的适宜的矿物组成材料和容易调模系度模数的水泥。在长期的施工经验中，有很多建筑单位在施工的过程中会选用热硅酸盐水泥和热矿渣水泥来用作建筑材料。
4.2大体积混凝土建筑中骨料的骨料的选配时要选用单粒直径大的粗骨料，骨料的直径越大其级配效果就越好，水泥的空隙就会减少。总表面积减少就会降低水泥的使用量，也就会降低混凝土的水热化现象了。
4.3参加适量的煤粉灰不仅能够降低生产成本减少对水泥的使用量，同时还能起到降低混凝土水热化现象的作用。粉煤中的硅、铝氧化物和三氧化二铝等物质可以和水泥中的水化物进行二次反应，在一定程度上减少了水泥使用量还能够避免混凝土出现膨胀现象。而且，混凝土和粉煤灰的二次反应可以让混凝土中的粉煤灰更加均匀的分布在其中。粉煤灰还具有进一步改善混凝土内部结构的功能，可以使内部成为孔状结构，总体结构也更加细密紧致了，混凝土的收缩值也相应的减少了许多。
4.4混凝土的浇灌对于大体积的混凝土技术也很重要。混凝土浇灌要严格按照“一个坡度、薄层浇筑，一次到顶”的浇灌原则进行浇灌施工。在浇筑的过程中还应该进行对混凝土的振捣操作，使得整体结构更加坚固密实，均匀一致。
5.总结
大体积混凝土技术作业是目前我国建筑施工中的一项新技术，只有在施工的过程中不断地摸索和掌握新的方法，运用有效的措施和科学方法，细心落实和监控各个重要的环节，就会避免施工中的各种问题和困难。保温和保护大体积的混凝土施工也是整个建筑过程的重要环节，保温保护有利于提高混凝土块体承受温度应力时的抗裂能力，可以有效的防止或控制温度裂缝。只要我们善于观察和研究，大体积混凝土施工技术一定会日臻完美的。
[参考文献]
[1] 侯君伟．现浇混凝土建筑结构施工手册．机械工业出版社．2003
[2] 杨南方等．混凝土结构施工实用手册．中国建筑工业出版社．2001
[3] 陈文通. 基础大体积混凝土施工技术研究[J]. 科技资讯, 2010,(28)
[4] 吴昌盛. 浅析建筑工程中基础底板大体积混凝土施工技术应用[J]. 广东科技, 2009,(S1)
关键字：建筑工程；匹配；水化热；温度控制措施；大体积混凝土；施工技术；浇筑
Abstract:With the development of construction technology in our country, big city logo and high-rise building facilities is more and more, therefore, is applied in the architectural engineering and construction of large volume concrete is to be imperative. Unlike other concrete construction method, the construction of large volume concrete need to be more strict technical and process. The construction project, many are beginning to use the large volume concrete. However, we often can discover, cracks in the construction process of mass concrete is easy to the formation of fine. For the concrete cracks, there is the existence of quality problems, so to prevent, manage and control the necessary.
Keywords: building engineering; matching; hydration heat; temperature control; mass concrete; construction technology; concrete
中图分类号：TV544+.91文献标识码：A文章编号：
1.在工程结构中大体积混凝土是整个建筑的基础，对于大型建筑有著很重要的作用，但是在混凝土的配置过程中如果不能合理的适当的处理混凝土水化热所引起的温度作用和混凝土自身的收缩膨胀等变形而产生的较大的温度应力，设计施工就可能会产生极具危害性的裂缝。
1.1在我国过去经常采取在建筑的过程中设置伸缩缝或者后浇带的方法来解决大体积混凝土的出现裂缝的现象。但是，随着建筑的发展，建筑工期的要求，以及由于建筑自身结构的整体性、功能性的客观要求等，现在很多企业对于这类建筑要求无缝施工。所以，我们不得研究和探讨如何在施工中不设置伸缩缝和后浇带也能够满足大体积混凝土建筑的设计和工程质量的要求。
1.2在国内对于大体积混凝土的定义中，机考虑了混凝土的几何尺寸，同时也考虑了由于在配置大体积混凝土的过程中因为水化热而引起的体积变化和裂缝问题。
1.3对于大体积混凝土目前国际上也没有统一的定义，在美国混凝土学会认为大体积混凝土是“现场浇筑的混凝土，尽最大到需要采取措施降低水化热和水化热引起的体积变化。以最大限度地减少混凝土的开裂。”这说明了在大体积混凝土的混凝土的建筑过程中由于水化热而引起的体积变化和开裂问题是其中最主要的和最需要想办法解决的技术问题。
2.现代的建筑中，时常会涉及到大体积的混凝土的施工，例如高层楼房的基础、大型设备基础或者水利大坝等等。大体积混凝土施工都有哪些特点呢。
2.1大体积混凝土的最主要的特点就是体积大，一般实体最小尺寸大于或等于1m，同时水化热引起混凝土内部的最高温度与外界气温之差预计超过25℃的混凝土。
2.2表面系数比较小，水泥水化热释放比较集中，内部温升比较快，所以大体积混凝土内外温差较大。
2.3大体积混凝土结构的几何尺寸较大,且必须采用技术措施以避免水泥水化热及体积变化引起裂缝的结构，其结构尺寸已经大到必须采取相应的技术措施,妥善处理温度差值、合理解决温度应力、并按裂缝开展进行处理及控制的混凝土施工技术。
3.首先就是要科学合理的做到大体积混凝土的配合比。在大体积混凝土的施工过程中，水凝水化时会产生一定温度的水化热，从而引起水泥温度的上升，但是温度上升的部位和程度都是不一样的，从而引起混凝土不同部位的温差可能会过大，温度应力如果超过了混凝土的抗拉强度就会导致混泥土随后出现细小的裂缝。
3.1刚才我们已经说过，大体积混凝土出现裂缝的一个主要原因就是水泥水化的过程中会产生水化热，而水化热引起的温差会导致混凝土开裂，所以在保证混凝土的质量的前提下降低单位水泥的比例，降低水泥用量是控制水化热所产生的温度的一项很重要的措施。
3.2也可以在配置水泥的过程中加入适量的粉煤灰，粉煤灰会有效的延缓混凝土配置在中所产生的水化热的释放时间，这样一来对于大体积的混凝土的温度的控制是很有利的。同时，在大体积混凝土中掺入粉煤灰还可以增强混凝土的后期强度，有效的保证提高混凝土强度，可以取得一举两得的效果。
3.3NF型缓凝高效减水剂是对大体积混凝土进行温控的最有力的外加剂之一。使用缓凝型外加剂可以有效的控制和延缓配置水泥过程中的所产生的水化热的释放时间，可以有效地降低混凝土在某一瞬间温度会和高很高，而是水化热的释放就会变得比较的平缓，这样就可以有效的避免由于水化热而导致的温差过大的现象。
3.4大体积混凝土开裂的原因除了是有于配置混凝土的过程中水化热所长生的温度造成的之外，还有一个重要的原因是由于所选用的水泥的种类和质量，所以，在建筑工程的过程中国，一定要选用优质的水泥。
3.5也可以通过改善混凝土的体积的稳定性来提高混凝土的抗裂性能，例如在配置混凝土的过程中掺入一定量的粗骨料就可以有效的改善混凝土的抗裂能力；也可以在保证混凝土的强度和施工方便的前提之下降低混凝土的含砂率，从而减少出现裂缝的可能性。
3.6外界的气候变化也是重要的影响因素之一。大体积混凝土在施工的过程中，外界的气温的变化对于混凝土的影响是很大很明显的。外界气温升高和气温的降低，都会带动大体积的混凝土的温度的升高和降低。特别是外界气温的骤降，就会增加整体的大体积的混凝土的外部和内部的温度梯度，这对于大体积混凝土的凝结和长久使用是很不利的一件事情。
4.建筑是由各种各样的建筑材料来完成的，所以选用合适的建筑材料是很重要的，只有选用正确的建筑材料，才能更好地解决建筑工程中所遇到的各种的问题。对于大体积混凝土施工技术而言，选择合适的建筑材料和正确的施工技术同样的重要。
4.1大体积混凝土首要要考虑的就是水泥的选用了。水泥之所以会造成温差，主要的原因是由于水泥在配置的过程中由于水热化而产生的。因此，减小温差的一个重要的办法就是尽量的避免混凝土的水热化现象，为了避免水热化现象的出现，可以选用具有早期水热化低的水泥材料。水泥出现水热化的原因是由于矿物成分和细度的函数，所以降低水泥的水热化现象可以可以选择何有一定量的适宜的矿物组成材料和容易调模系度模数的水泥。在长期的施工经验中，有很多建筑单位在施工的过程中会选用热硅酸盐水泥和热矿渣水泥来用作建筑材料。
4.2大体积混凝土建筑中骨料的骨料的选配时要选用单粒直径大的粗骨料，骨料的直径越大其级配效果就越好，水泥的空隙就会减少。总表面积减少就会降低水泥的使用量，也就会降低混凝土的水热化现象了。
4.3参加适量的煤粉灰不仅能够降低生产成本减少对水泥的使用量，同时还能起到降低混凝土水热化现象的作用。粉煤中的硅、铝氧化物和三氧化二铝等物质可以和水泥中的水化物进行二次反应，在一定程度上减少了水泥使用量还能够避免混凝土出现膨胀现象。而且，混凝土和粉煤灰的二次反应可以让混凝土中的粉煤灰更加均匀的分布在其中。粉煤灰还具有进一步改善混凝土内部结构的功能，可以使内部成为孔状结构，总体结构也更加细密紧致了，混凝土的收缩值也相应的减少了许多。
4.4混凝土的浇灌对于大体积的混凝土技术也很重要。混凝土浇灌要严格按照“一个坡度、薄层浇筑，一次到顶”的浇灌原则进行浇灌施工。在浇筑的过程中还应该进行对混凝土的振捣操作，使得整体结构更加坚固密实，均匀一致。
5.总结
大体积混凝土技术作业是目前我国建筑施工中的一项新技术，只有在施工的过程中不断地摸索和掌握新的方法，运用有效的措施和科学方法，细心落实和监控各个重要的环节，就会避免施工中的各种问题和困难。保温和保护大体积的混凝土施工也是整个建筑过程的重要环节，保温保护有利于提高混凝土块体承受温度应力时的抗裂能力，可以有效的防止或控制温度裂缝。只要我们善于观察和研究，大体积混凝土施工技术一定会日臻完美的。