论文部分内容阅读
报道了常压金属有机化学汽相淀积（ＭＯＣＶＤ）制备的Ｚｎ０．７Ｃｄ０．３Ｓｅ／ＺｎＳｅ单量子阱的光泵浦受激发射性质。在７７Ｋ下观测到了ｎ＝２的重空穴激子发光峰和ｎ＝１的重空穴激子吸收峰。在７７Ｋ脉冲激光泵浦下受激发射阈值功率密度为１１６ｋｗ／ｃｍ２。认为受激发射机理可能是激子局域态的空间填充。
Reported the optically pumped stimulated emission properties of Zn0.7Cd0.3Se / ZnSe single quantum well prepared by atmospheric pressure metal-organic chemical vapor deposition (MOCVD). The heavy hole exciton emission peak with n = 2 and the heavy hole exciton absorption peak with n = 1 were observed at 77K. The stimulated emission threshold power density was 116kw / cm2 at 77K pulsed laser pumping. It is considered that the stimulated emission mechanism may be the spatial filling of exciton local states.