【摘 要】
：
The Lap-joint configuration and the vacuum assisted forming method were put forward to meet the demands of the compression bending strength and the strong connection between the steel and FRC.The bending mechanic tests of the Lap-joint bending specimens c
【机 构】
：
School of Science, Wuhan University of Technology, Wuhan 430070, China;Wuhan Institute of Marine Ele
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The Lap-joint configuration and the vacuum assisted forming method were put forward to meet the demands of the compression bending strength and the strong connection between the steel and FRC.The bending mechanic tests of the Lap-joint bending specimens carried out, the fabricate processing stability, limit carrying capacity and failure modes were analyzed. The experimental results show that the fabricate processing of the Lap-joint is stable; the bending stiffness is 19.5 N/mm, and the limit bending moment reaches 318 N·m. The main failure modes are the failure of core material at junction of sandwich plate and steel, and the bending failure in the position of the inner and outer surface.
其他文献
The effects of Cr3+,Cu2+,and Pb2+ on compressive strength,reaction products,and pore structures of fly ash based geopolymer were studied.In addition,the immobilization and bonding interaction between heavy metal and fly ash based geopolymers were investig
Plasma-enhanced CVD (PECVD) epitaxy at 200 oC was used to deposit heavy doped n-type silicon films. Post-annealing by rapid thermal processing was applied to improve the properties of the epitaxial layer. By analyzing the Raman spectra and the imaginary p
In order to investigate how to enhance the teeth fracture resistance after the post and core treatment, an in vitro study was conducted to measure the fracture resistance of endodontically treated teeth restored with cast post and core with two kinds of s
The effect of spherical particle size on the surface morphology, electrochemical property and processability of lithium iron phosphate was systematically studied. Spherical lithium iron phosphate with different particle size distributions controlled with
A modified co-precipitation method for the production of Cu/ZnO/Al2O3 complex was studied. The modification was that part of Al was introduced by adding Al3+ into Cu2+/Zn2+ solution, and the rest of Al was added after co-precipitation step in the form of
A new method of fabricating C/C composite materials, namely electric heating CVD method, was used, which electrified the carbon fiber directly by using the conductivity of itself. Acetylene was used as the carbon source with nitrogen as dilution gas, and
Zn2SnO4/few-layer boron nitride nanosheets (FBNNS) hybrids were synthesized via a one-step hydrothermal method. The structures, morphology, optical properties, electron transformation and separation of the as-prepared products were characterized by X-ray
The rare earth doped TiO2 was prepared and characterized with Nd,Ho and Y as the doping agents,which have obvious absorption in visible light area.The particle size of the glomeration was about 200-400 nm.TiO2 sensor performed a significant change in resi
Red mud was firstly used as a raw material in sintering field road cement. Then, the radioactive element distribution characteristics of red mud based field road cement (RFC) before and after hydration were comparatively investigated. The experimental res
Phase pure ZrB2-SiC composite powders were prepared after 1 450 ℃/3 h via carbothermal reduction route,by using ZrSiO4,B2O3 and carbon as the raw materials.The influences of firing temperature as well as the type and amount of additive on the phase compos