【摘 要】
：
The high strength bridge steel was processed with the simulated coarse grain heat affected zone (CGHAZ) thermal cycle with heat input varying from 30 to 60 kJ/cm, the microstructures were investigated by means of optical microscope (OM), scanning electron
【机 构】
：
State Key Laboratory of Materials Processing and Die & Mould Technology, School of Materials Science
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The high strength bridge steel was processed with the simulated coarse grain heat affected zone (CGHAZ) thermal cycle with heat input varying from 30 to 60 kJ/cm, the microstructures were investigated by means of optical microscope (OM), scanning electron microscope (SEM), electron backscattering diffraction (EBSD) and transmission electron microscope (TEM), and the impact properties were evaluated from the welding thermal cycle treated samples. The results indicate that the microstructure is primarily composed of lath bainite. With decreasing heat input, both bainite packet and block are significantly refined, and the toughness has an increasing tendency due to the grain refinement. The fracture surfaces all present cleavage or fracture for the samples with different heat inputs. Moreover, the average cleavage facet size for the CGHAZ is nearly equal to the average bainite packet size and the bainitic packet boundary can strongly impede the crack propagation, indicating that the bainitic packet is the most effective unit in control of impact toughness in the simulated CGHAZ of high strength bridge steel.
其他文献
Backscattered electron images (BSE) obtained by scanning electron microscope was used to quantitatively characterize the microstructure of interfacial transition zone (ITZ) in concrete. Influences of aggregate size (5, 10, 20, and 30 mm), water to cement
Vanadium trioxide (V2O3) was directly prepared by NaVO3 electrolysis in NaCl molten salts. Electrolysis products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The existing state
Yield stress development of cement paste is potentially governed by percolation of 3-dimensional links formed by hydration products on the surface of the particles. It rises steadily at a gradual rate before a sudden increase in rate of growth. In this st
Mg0.2Zn0.8O (MZO)/La0.67Ca0.33MnO (LCMO) heterostructure was deposited on p+-Si substrates by sol-gel spin coating technique.The Ag/MZO/LCMO/p+-Si devices exhibit a bipolar,reversible,and remarkable current-voltage characteristic at room temperature.An ob
Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity (Erd values) were mon
For refining grain and obtaining excellent properties,the experiments of asymmetric and symmetric monotonic hot roiling were carried out to investigate the role of shear strain on the microstruetures and mechanical properties of V-microalloyed steel.The s
The microstructure,tensilc property and wear resistance of 7075 aluminum matrix composite reinforced with TiC particles prepared by in-situ reaction casting were investigated.The effect of TiC reinforcement on wear behavior was analyzed.The wear mechanism
Graded porous scaffold can be applied to study the interactions between cells and scaffold with different pore sizes.Polydimethylsiloxane(PDMS)scaffold with an axial pore size grade was successfully manufactured via vacuum-assisted resin transfer moulding
We investigated the effects of different barium compounds on the thaumasite form of sulphate attack (TSA) resistance of cement-based materials when they were used as admixtures in mortars. Moreover, we analyzed the inhibition mechanisms within different t