The 500 MHz 5-cell superconducting RF(SRF) cavity was designed aiming to be a candidate cavity for high current accelerators. A copper prototype cavity and a niobium cavity were fabricated at SINAP in 2012. In order to ensure these cavities get the desired frequency and a good field flatness higher than 98%, frequency control was implemented in the manufacturing process and pre-tuning has been done using a simple pre-tuning frame based on the bead-pull pre-tuning method. Then, TM010-π mode frequency within 5 kHz from the target frequency was achieved and the field flatness reached 98.9% on the copper prototype cavity. Finally, the same procedure was applied to the niobium cavity to obtain a field flatness better than 98% which benefited the cavity performance in the vertical testing. The 500 MHz 5-cell superconducting RF (SRF) cavity was designed aiming to be a candidate cavity for high current accelerators. A copper prototype cavity and a niobium cavity were fabricated at SINAP in 2012. In order to ensure these cavities get the desired frequency and a good field flatness higher than 98%, frequency control was implemented in the manufacturing process and pre-tuning has been done using a simple pre-tuning frame based on the bead-pull pre-tuning method. Then, TM010-π mode frequency within 5 kHz from the target frequency was achieved and the field flatness reached 98.9% on the copper prototype cavity. Finally, the same procedure was applied to the niobium cavity to obtain a field flatness better than 98% which benefited the cavity performance in the vertical testing.