Effect of Submillimeter Variation in Plunge Depth on Microstructure and Mechanical Properties of FSL

来源 :金属学报(英文版) | 被引量 : 0次 | 上传用户:lupt2681006
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Friction stir lap welding was conducted on 2 mm + 2 mm sheets of aluminum alloy 2A12-T4.The plunge depth (PLD) was designed as 2.45-2.58 mm,which was varied in submillimeters as 2.45,2.50,2.53,2.55,and 2.58 mm,and the axial force was recorded in the welding process.The results show that the PLD fluctuation in submillimeters causes significant variation in the axial force and affects the voids (i.e.,Void Ⅰ and Void Ⅱ),hook,and effective sheet thickness (EST),among which Void I is the main factor that affects the EST.The fracture load-PLD function in the tensile shear test of the joints follows the rule of the EST-PLD function.An optimized PLD is approximately 2.55 mm,at which the EST reaches 1.71 mm,corresponding to a peak fracture load of 11.03 kN.Thus,a PLD of 2.55 mm is suggested with a tolerance of 0.02 mm,corresponding to a fracture load of 9.6-11.0 kN,i.e.,within a fluctuation of 12%.
其他文献
The influences of Mo contents on mechanical properties,biocorrosion and cytocompatibility of as-cast Mg-6Zn-8.16Y-2.02Mn-xMo (x =0.0,0.1,0.3,0.5,0.7 wt%) alloys were firstly investigated.Appropriate amount of Mo was conducive to grain refinement and the f
Refill friction stir spot welding was employed to produce 6061-T6 aluminum alloy joints with different sleeve plunge depths.The interface characteristics of joint-line remnant and hook are investigated by optical and scanning electron microscopy.The joint
Ni-W-TiC composite coatings were prepared via electrodeposition technique by dispersing the different amount of TiC particles into the plating bath.The Ni-W and Ni-W-TiC composite coatings containing different concentrations of TiC particles were characte
The consolidation recycled AZ80 billets were successfully fabricated through the cold press and hot press sintering of the AZ80 metal chips.The consolidation recycled billets sintered at 350 ℃ present the comparable compressive properties and inferior ten
Finite element simulations for metal powder compaction of a clutch plate were performed to examine the stresses during compaction,unloading,and ejection.To describe the mechanical behavior of compacted green body,a modified densitydependent Drucker-Prager
To improve the corrosion resistance of friction stir welded (FSW) joints,in situ shot-peening-assisted cold spray coating was applied to the surface of FSW joints.The microstructure and corrosion behavior of the coatings were investigated.The results show
Titanium alloy Ti-Al-Nb-Zr has high specific strength and becomes a promising structural material used in the deep sea.The excellent corrosion resistance of the alloy is derived from the protective passive film formed on its surface.By now,full agreement
Cu pillar bump offers a number of advantages for flip chip packaging,compared to the conventional solder bump.However,due to its rigidity structure,Cu pillar bump introduces a lot of stress to the chip,which causes the failure of packaging structures,espe
Microalloying is an effective method to improve the comprehensive properties of copper alloys.The effects of magnesium on the microstructure,mechanical properties and anti-stress relaxation properties of CuNiSi alloys have been investigated.Results demons
Structural metallic materials with excellent functional performance and lightweight features have always been the goal of material scientists\' pursuit.In this work,laminated metal composites of different thicknesses (less than 0.4 mm) composed of struc