本文研究了原始组织对T10钢的球化率及碳化物粒度的影响。结果表明,随着原始组织的珠光体片的细化,球化退火后的球化率增高;碳化物粒度细小。
In this paper, the effect of primary structure on the spheroidization rate and carbide particle size of T10 steel was studied. The results show that with the refinement of the pearlite sheet of the original structure, the spheroidization rate increases after spheroidizing annealing and the carbide particle size is small.