【摘 要】
：
采用超声振动辅助搅拌法制备Mg-6Zn-1Y-0.2Co-0.1Sc镁合金,利用X-射线衍射仪、扫描电子显微镜、能谱分析仪和力学性能试验机等分析测试手段,研究其微观组织与低温拉伸性能。
论文部分内容阅读
采用超声振动辅助搅拌法制备Mg-6Zn-1Y-0.2Co-0.1Sc镁合金,利用X-射线衍射仪、扫描电子显微镜、能谱分析仪和力学性能试验机等分析测试手段,研究其微观组织与低温拉伸性能。结果表明,Mg-6Zn-1Y-0.2Co-0.1Sc镁合金由α-Mg基体和少量Mg3YZn6和Mg3Y2Zn3相组成。随着温度的降低,合金的抗拉强度和屈服强度逐渐增加,伸长率逐渐降低。
The Mg-6Zn-1Y-0.2Co-0.1Sc magnesium alloy was prepared by ultrasonic vibration assisted stirring method. The microstructure was studied by means of X-ray diffraction, scanning electron microscopy, With low temperature tensile properties. The results show that Mg-6Zn-1Y-0.2Co-0.1Sc magnesium alloy consists of α-Mg matrix and a small amount of Mg3YZn6 and Mg3Y2Zn3 phases. As the temperature decreases, the tensile strength and yield strength of the alloy gradually increase, and the elongation decreases gradually.
其他文献
Aer Met100 ultra-high strength steel plates with a thickness of 2 mm were welded using a CO2 laser welding system. The influences of the welding process paramet
采用高真空高纯氩DSC测量了(Nd,Pr)12.8Dy0.2Fe77.4Co4.0B5.6非晶快淬薄带以及不同温度退火薄带的连续加热曲线,计算了晶化激活能、频率因子、晶化体积分数、晶化速率,研究了
目的:探讨心肌酶谱检测在急性心肌梗死患者中的临床效果.方法:选取2019年1月—2020年1月期间到本院治疗的50例急性心肌梗死患者进行前瞻性分析,并将其设为研究组;选取同期在
因为沿岸可用的土地面积越来越少且价格越来越高，所以，应用离岸人工岛作为工业场地和深水港口的要求在不断增加．本文对人工岛的选址因素进行了评述．另外，还介绍了已经建成或计划建
针对铁模铸造镁阳极出现的钢芯不居中、晶粒粗大、杂质元素含量过高、偏析、气孔、缩孔、裂纹、多肉、冷隔等缺陷的成因进行分析,并提出相应的防治措施。
According to the
目的:探讨在规培护士阶段化考核中采取OSCE的效果.方法:纳入时间为2017年1月至2018年1月,选取我院规培护士50例,分组方法为随机数字表法,各25例.对参照组采取常规考核,对实验
国际地圈生物圈计划的核心计划之一是海岸带海陆相互作用（ＬＯＩＣＺ），“海岸带海陆相互作用”中国工作组已经成立，为参与全球变化的研究，需要选择海陆相互作用明显，影响又大的地区进行研究，以
目的:探析细节护理在肿瘤放疗中的应用对生活质量所造成的影响.方法:60例肿瘤患者随机分为观察组和对照组,每组30例.对照组采取常规护理,观察组患者应用细节护理,比较两组的
介绍了冷轧薄规格(厚度≤0.2 mm)产品的生产工艺及现状。重点对生产过程中影响钢卷板面质量的因素进行了分析,制定出多项控制措施:控制酸洗工艺指标,及时更换衬胶辊系;轧制过
通过对黄、东海海域底质沉积物中的细粒级粘土矿物组合特征和全粒级碳酸盐含量分析、对比上覆水团和悬浮体资料，探讨研究区水团发育消长对底质沉积物分布的影响作用。结果表明