The effect of heat treatment on the microstructures and mechanical properties of a newly developed austenitic heat resistant steel (named as T8 alloy) for ultra-supercritical applications have been studied.Results show that the main phases in the alloy af
【机 构】
：
Institute of Metal Research, Chinese Academy of Sciences,Shenyang 110016, China;School of Materials
论文部分内容阅读
The effect of heat treatment on the microstructures and mechanical properties of a newly developed austenitic heat resistant steel (named as T8 alloy) for ultra-supercritical applications have been studied.Results show that the main phases in the alloy after solution treatment are γ and primary MX.Subsequent aging treatment causes the precipitation of M23C6 carbides along the grain boundaries and a small number of nanoscale MX inside the grains.In addition,with increasing the aging temperature and time,the morphology of M23C6 carbides changes from semi-continuous chain to continuous network.Compared with a commercial HR3C alloy,T8 alloy has comparable tensile strength,but higher stress rupture strength.The dominant cracking mechanism of the alloy during tensile test at room temperature is transgranular,while at high temperature,intergranular cracking becomes the main cracking mode,which may be caused by the precipitation of continuous M23C6 carbides along the grain boundaries.Typical intergranular cracking is the dominant cracking mode of the alloy at all stress rupture tests.
其他文献
Using both numerical and experimental methods,we studied the effect of coil configuration of pulsed magneto-oscillation (PMO) on distribution of electromagnetic field,flow field and solidification structure with the same pulse current parameters in Al ing
Hot deformation behavior, microstructural evolution and flow softening mechanism were investigated in Ti-46Al-8Nb alloy via isothermal compression approach. The true stress-strain curves exhibited typical work hardening and flow softening, in which the de
Ultra-strong joints of pure Cu and Cu-30Zn alloy were obtained by friction stir welding under flowing water.The effects of heat inputting condition and material characteristics on the morphologies,microstructures and mechanical properties of welding joint
In this study,shot peening is applied to the titanium alloy Ti-6Al-4V,and the surface treatment effect on fatigue life of shot-peened specimens under high cycle loading is investigated.The induced residual stress is measured by using the orbital hole-dril
Degradation behaviors of three typical La-Mg-Ni alloys,La2MgNi9,La1.5Mg0.5Ni7 and La4MgNi19,were studied.La1.5Mg0.5Ni7 with (La,Mg)2Ni7 as main phase presents better discharge capacity and cycling stability.The three alloys suffer severe pulverization and
Homogenization of physical properties and the chemical composition through the control of liquid metal flow is essential during the continuous casting production of billets.This work was aimed at obtaining improved finished products via continuous casting
In the present work,a CuCrZr alloy characterized by ultrafine grains and nanoscale particles was prepared by equalchannel angular pressing (ECAP) at 450 C.A desired combination of a tensile strength (580 MPa) and an electrical conductivity (81％ Internatio
The microstructure and stress-rupture property of the large-scale complex single crystal (SX) casting DD10 were investigated in high-rate solidification process.It is found that the primary dendrite arm spacing (PDAS) does not increase monotonically with
The reliability of a substrate curvature-based stress measurement method for CrN thin films on substrate with fluctuant surface was discussed.The stress error led by the ignorance of substrate thermal deformation was studied.Results showed that this error
Using the methods of transmission electron microscopy,the carbide phase evolution in surface layers of the differentially quenched rails is studied after the passed tonnage of 691.8 million tons at the depth up to 10 mm along the central axis and fillet o