Nd doped multiferroic BiFeO3 (Bi0.94Nd0.06FeO3 (BNF)) nanotubes were successfully synthesized by a sol-gel template method.Electron microscopy investigations exhibited that these nanotubes had straight and smooth profile with diameters of about 200 nm and wall thickness of about 20 nm.A perovskite-type structure of BNF was confirmed in the nanotubes by high-resolution transmission electron microscopy and selected area electron diffraction analysis.These nanotubes had high resistivity.The dielectric constant and dielectric loss of the nanotubes were 126 and 0.040 at 1 MHz, respectively.The ferroelectric properties of these BNF nanotubes were demonstrated with a remnant polarization of 48 μC/cm2 and a coercive electric field of 163 kV/cm.
Nd doped multiferroic BiFeO3 (Bi0.94Nd0.06FeO3 (BNF)) nanotubes were synthesized synthetically by a sol-gel template method. Electron microscopy investigations showed that those nanotubes had straight and smooth profiles with diameters of about 200 nm and wall thickness of about 20 nm.A perovskite-type structure of BNF was confirmed in the nanotubes by high-resolution transmission electron microscopy and selected area electron diffraction analysis. These nanotubes had high resistivity. The dielectric constant and dielectric loss of the nanotubes were 126 and 0.040 at 1 MHz , respectively.The ferroelectric properties of these BNF nanotubes were demonstrated with a remnant polarization of 48 μC / cm2 and a coercive electric field of 163 kV / cm.