Can the Prior Cathodic Polarisation Treatment Remove the Air-Formed Surface Film and Is It Necessary

来源 :金属学报(英文版) | 被引量 : 0次 | 上传用户:zhucejuren2011
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
This paper clarifies two issues related to the prior cathodic polarisation treatment (PCPT) for the potentiodynamic polarisation test: whether PCPT can (1) remove the air-formed surface film and (2) affect the polarisation test results.X-ray photoelectron spectroscopy analyses of fluoride ion-labelled samples show that PCPT cannot remove the surface film completely due to the low reaction rate.Potentiodynamic polarisation tests demonstrate that PCPT with proper operating parameters,-1.0 VscE for 5 min with subsequent open circuit potential (OCP) stabilisation in this study,is necessary because it can improve the test reproducibility without affecting the corrosion parameters by unifying the initial surface state.However,PCPT with lower potentials,longer time or no OCP stabilisation has significant effects on the electrochemical corrosion parameters due to the hydrogen absorption under the conditions of this study.
其他文献
In the present study,the weld formation and mechanical properties of the AA-5A06 friction pull plug welded (FPPW) joints were improved by controlling the axial force history.Several defect-free FPPW joints were made successfully by using the welding param
A 17 vol% SiCp/Al-Mg-Si-Cu composite plate with a thickness of 3 mm was successfully friction stir welded (FSWed) at a very high welding speed of 2000 mm/min for the first time.Microstructural observation indicated that the coarsening of the precipitates
In the present experimental investigation,Al-3 wt%Cu and A1-3 wt%Cu-0.5 wt%Mg alloys castings are produced by a horizontal solidification technique with a view to examining the interrelationship among growth rate (GR),cooling rate (CR),secondary dendrite
In this study,near fully dense (96.5%) pure tungsten bulks were additively manufactured and the cracking behavior was investigated.A crack network with a spacing of ~ 100 μm was observed in the fabricated bulks.It was observed that the laser scanning stra
Fe-10 at.%Cr alloy was implanted with hydrogen ions at room temperature,followed by annealing at high temperatures.The annealing process made the defects develop into large dislocation loops.The nature of the dislocation loops formed after annealing was s
The work is mainly to study the thermal stability including the phase stability,microstructure and tribo-mechanical properties of the A1B2-type WB2 and W-B-N (5.6 at.% N) films annealed in vacuum at various temperatures,which are deposited on Si and GY8 s
The dynamic mechanical relaxation behavior of Ti36.2Zr30.3Cu8.3Fe4Be21.2 bulk metallic glass with good glass-forming ability was investigated by mechanical spectroscopy.The mechanical relaxation behavior was analyzed in the framework of quasi-point defect
CoFe2O4 nanoparticles (NPs) and surface modified with gold (Au) have been synthesized by a thermal decomposition method.The obtained NPs and formation of CoFe2O4@Au core-shell (CS) were confirmed by characterizing their structural and optical properties u
Plasma nitriding is a widely used technology to enhance the surface performance and extend the service life of alloy parts.The current research mainly focuses on the influences of time,temperature,gas type and pressure parameters on nitriding behavior,whi