Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of NaCI deposition increases with the exposure time, which can be correlated by using exponential decay function. The relationship between dry mass gain and amount of NaCI deposition at a certain exposure time follows a quadratic function. More amount of NaCI deposition will slow down the corrosion rate to some extent after exposure for a certain time. SEM/EDAX was used to characterize the corrosion surface and products. The surfaces of the NaCI treated A3 steel were obviously uneven, and some tiny crevices appear in the corrosion products that could help O2 transmit to the inner layer. The amount of oxygen in atomic percentage in the corrosion products increases with the amount of NaCI deposition.
Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of NaCI deposition increases with the exposure time, which can The correlated between dry mass gain and amount of NaCI deposition at a certain exposure time follows a quadratic function. More amount of NaCI deposition will slow down the corrosion rate to some extent after exposure for a certain time. SEM / EDAX was used to characterize the corrosion surface and products. The surfaces of the NaCI treated A3 steel were very significant, and some tiny crevices appear in the corrosion products that could help O2 transmit to the inner layer. The amount of oxygen in atomic percentage in the corrosion products increases with the amount of NaCI deposition.