通过热模拟实验,研究了冷却工艺参数对Ti微合金化高强钢组织和硬度的影响.结果表明:当终冷温度为700℃时,随着冷却速度的增大,铁素体和珠光体组织得到了显著细化,实验钢硬度
Vanadium-bearing titanomagnetite carbon composite briquette (VTM-CCB) was proposed as an innovative and promising blast furnace burden to realize low-carbon and
以β-环糊精为壁材、桉叶精油为芯材,通过冷冻干燥法制备用于纺织品芳香及抗菌整理的桉叶精油微胶囊,分析壁芯比、包埋温度和包埋时间对桉叶精油微胶囊包埋率的影响。通过正交试验确定最佳工艺条件为β-CD浓度8g/mL、包埋温度40℃、包埋时间2h。在该条件下桉叶精油微胶囊的包埋率为72.68%,包埋效果较好。
The effects of 0.01–0.11 wt.％Zr on the inclusions, microstructure, tensile properties, and impact toughness of the China low activation martensitic steel were i
The influences of superheat and cooling intensity on macrostructure and macrosegregation of one new kind duplex stainless steel (DSS) were studied. Thermal simu
Closing a single nozzle or multiple nozzles for a temporary casting operation (fewer strands casting) was common in a tundish due to insufficient molten steel o
为提高钢水质量,降低吨钢成本,减少转炉渣的影响,众多钢厂采用转炉滑板挡渣系统。在这套系统中,转炉挡渣滑板是耐材的核心,滑板寿命影响到系统的更换频率、生产节奏等。通过了解和研究现场挡渣滑板粘渣、夹钢等问题,发现内滑板和外滑板的损毁是不同部位和不同状态,分析了转炉挡渣滑板损毁机理。以现有转炉挡渣滑板材质工艺为基础,分别对内滑板进行了工艺改进,对外滑板进行材质开发和工艺改进。现场使用表明,在其他条件不变的情况下,改进的转炉挡渣滑板比原滑板使用次数大幅提高。
为了弄清MgO不同粒度组成对组织脆化的影响,对1.0 mm以下的MgO进行分级筛分,制备了不同粒度组成的试样,并进行了评价.结果发现:随着MgO表面积的增加,质量损失率加大,伴随着反
100%亚麻梭织布经过阳离子改性处理后,以金属络合染料做浸轧染色,最终形成“环染”的效果,再经过后续的固色处理,达到需要的色牢度,经制成成衣后再经过成衣酵洗工艺处理,呈现出独特的“仿旧”风格。同时还结合亚麻特色,对于亚麻成衣的手感整理也做了探讨,使之既保持亚麻面料的独特风格,又赋予亚麻面料以舒适的手感,提高了其服用性能。
以电炉粉尘(EAFD)中提取的Zn2+、铁鳞中提取的Fe3+和六水合氯化镍(NiCl2·6 H2 O)为原料,采用水热法直接制备合成尖晶石型Ni-ZnFe2 O4.首先探讨了焙烧温度、NaOH与EAFD质量比