【摘 要】
：
通过熔铸法原位合成了(Ti3Sn+Ti5Si3)增强Ti基复合材料,利用扫描电镜观察了包含相间隔的细晶粒Ti基体与Ti3Sn和Ti与Ti5Si3组成的共晶组织。对试样进行室温下的压缩性能测试,
论文部分内容阅读
通过熔铸法原位合成了(Ti3Sn+Ti5Si3)增强Ti基复合材料,利用扫描电镜观察了包含相间隔的细晶粒Ti基体与Ti3Sn和Ti与Ti5Si3组成的共晶组织。对试样进行室温下的压缩性能测试,结果表明,随着Sn含量的增加,试样的杨氏模量和耐压强度都比Ti-Si合金高;当Sn含量达到25wt%时,试样的杨氏模量和耐压强度降低,但压缩率有所升高。
The (Ti3Sn + Ti5Si3) reinforced Ti matrix composites were synthesized by in-situ casting method. The eutectic microstructure composed of fine-grained Ti matrix with Ti3Sn and Ti and Ti5Si3 was observed by scanning electron microscopy. The compressive properties of the samples were tested at room temperature. The results show that with the increase of Sn content, the Young’s modulus and compressive strength of the samples are higher than that of Ti-Si alloy. When the Sn content reaches 25wt% Young’s modulus and compressive strength decreased, but the compression rate increased.
其他文献
据一家叫IMC-Agrico的公司在英特网上介绍,他们开发出一种称做超级尿素的新化肥品种.超级尿素是一种兰色粒状化肥,是用氨和二氧化碳在高压下反应而生成的.超级尿素含有(N-丁
结合混凝土材料的缺陷分析,探讨了含沙高速水流冲击作用下,混凝土材料的冲蚀磨损特性与机制.结果表明,混凝土材料呈现典型的脆性材料磨损特征,冲击角度较低时,硬质磨粒的切削
采用水热合成法，合成了CO、Cu掺杂的MCM-41介孔分子筛，并以NaoH为促进剂用于大豆油和甲醇酯交换制备生物柴油。结果显示，si/CO为20时产率达95％，Si/Cu为20时反应产率达80％，且生物柴油
密胺纤维是美国巴斯夫公司开发出的三胺后加工新产品,并已投入商业化生产.
印度快讯(India Express Network)在英特网上公布了印度在2000～2025年间的化肥工业发展方针.据比较保守的估计,到2025年印度每年需要生产301 Mt粮食才能满足其10亿人口的需要,
2017年6月30日,我受聘为山东农业大学特聘教授。在受聘仪式上,面对200多名师生,我做了《“丝路天马”的传承与创新》主题演讲。从汉画像石到大苑名马,从赤兔马到飒露紫,从幼
按CNG/汽油两用燃料发动机对机油清净分散性能要求,选择了几种清净分散剂,通过试验考察了基础油与添加剂的感受性,采用均匀设计分析了几种添加剂之间的复配性能.试验结果表明
采用乙醇作为反应介质,将氨水滴入硝酸铝乙醇溶液中进行中和反应,经洗涤、过滤和烘干后得到氢氧化铝超细粉。将制得的超细氢氧化铝粉与铁粉按一定比例充分混合,经压制、烧结
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
著名的木桶理论认为:一只木桶盛水的多少,并不取决于桶壁上最高的那块木块,而恰恰取决于桶壁上最短的那块.同样,对于一所学校、一个班级而言,后进生群体就是那块最短的木块,