论文部分内容阅读
摘要：建筑屋面按其坡度一般可分为平屋面和坡屋面，其中坡屋面由于具有坡度大、屋面不易积水、屋顶阳光照射角度大、立面美观丰富等特点，近年来被广泛采用。但一些坡屋面在竣工时或在使用一两年后，常会发生渗漏现象，渗漏部位多为屋面交接处、山墙边、枪沟底等处，影响建筑的正常使用和美观。本文主要就混凝土坡屋面的渗漏原因及防治对策做了深入探讨。
关键词：坡屋面；渗漏；结构；防水材料；模板
Abstract: the roof according to their grade generally can be divided into flat roof and slope roof, which because of the large slope, slope roofing roofing not easy seeper, roof sun Angle is large, rich facade is beautiful wait for a characteristic, is widely used in recent years. But some slope roof in the completion, or in the use of one or two years later, often happen leakage, leakage of parts for roofing junction, gable side, the place such as gun groove, affect the normal use of buildings and beautiful. This article mainly concrete slope roof leakage causes and countermeasures for the further discuss.
Key words: slope roof; Leakage; Structure; Waterproof material; The template
中圖分类号： TV697.3+2 文献标识码：A文章编号：2095-2104(2013)
坡屋面的构造特点
目前最常用的是大面积现浇钢筋混凝土坡屋面，一般其从下至上大致可分为：结构层、找平层、防水隔热层、屋面瓦等4大构造层，各构造层的质量好坏都与屋面渗漏与否密切相关。
（一）结构层
现浇钢筋混凝土板，是屋面的主体结构。屋面防水效果的关键就在于结构层能否起到防水作用，混凝土的施工质量、是否密实、有否裂缝及钢筋架设是否合理等都直接影响屋面的防水效果。
（二）找平层
用以找平结构，形成坚硬平整表面，以便防水隔热层的施工，找平层施工时的质量好坏，将直接影响到防水隔热层的质量。
（三）防水隔热层
其实是隔热层和防水层2层，质量与各自的施工工艺及材料好坏有很大关系，如果质量不佳产生裂缝会导致屋面渗漏。
（四）屋面瓦
贴于坡屋面外表面，起到美化立面及防水、防渗作用。若瓦片抗渗、抗冻、吸水等性能不佳，尺寸控制不严，瓦接缝不严等都会造成屋面渗漏。
混凝土坡屋面的渗漏原因分析
（一）构造原因
坡屋顶形式多样、结构复杂，变坡转折处、结构交接面和细部节点比较多。对屋面板来说，这些都是支座部位，其实际受力情况因该处构造的不同而复杂多样，结构设计计算时假定的约束形式与实际存在一定的差异，而且，各面受力变形情况不一致，会导致交接处的应力集中，设计配置的构造钢筋往往不能抵抗该处板块受力产生的弯矩而发生了裂缝。同时，这些部位的防水设防施工困难，不同防水材料的性能差异使交接处的节点处理难度加大，增大屋面渗水的可能性。
（二）材料原因
1、混凝土
混凝土是一种非均匀材料，内部分布着大量的微小孔隙；材性上其抗拉强度较低，受拉时易出现裂缝；屋面露天受气候影响大，易热胀冷缩产生温度裂缝；屋面板在长期使用中发生徐变，也会引起结构裂缝，这些都易形成渗水通道。
2、防水材料
防水材料的选择也至关重要。当屋面坡度较大时，使用防水卷材施工不方便，容易下滑；节点细部采用卷材防水块材较小、搭接面多，无法保证枯贴质量。而在一些屋面板交接面变形较大，局部需要增设防水加强层，而此处使用防水涂膜施工层次较多，湿作业施工容易造成涂料流淌，施工进度慢，难以保证加强层厚度。
屋面瓦
屋面瓦是直接与雨水和大气接触的层面，若施工中瓦的材质不保证，存在砂眼裂缝孔洞现象；或者瓦片在常年的日晒雨淋作用下产生微细裂纹，会使瓦片本身的防水能力下降甚至丧失。此外，屋面瓦块体铺设的接缝太多，施工中不能保证瓦层的整体性，尤其在暴风雨和台风时易发生渗漏。
（三）施工原因
1、混凝土坍落度控制不当
坍落度过小，影响施工操作，混凝土不易振实，造成屋面渗漏；坍落度过大，混凝土内部多余水分蒸发后会形成微小空隙，容易连通形成毛细孔隙，成为雨水渗入的通道。
施工缝位置留设不当
若将施工缝留设在屋脊、屋面变坡处等结构应力转换处，容易产生裂缝。
细部处理欠妥
坡屋面往往形式较复杂、交接面多、节点多，这些部位钢筋绑扎及混凝土振捣都较困难，而且属于应力集中区域，施工不好则会使混凝土开裂。另外，屋面常有一些如排风道、下水管、天沟等的附加设施，施工处理不好很容易引起渗漏。
施工方法不当
有些坡度大于 30°的屋面仍采用地板支模，易造成施工质量事故；局部板厚不满足要求会使结构出现裂缝；钢筋配置不到位，负筋易被踩低，无法与混凝土一起抵抗弯矩而使板产生裂缝。
房屋交付使用后安装太阳能等设施，容易破坏防水层，使屋面漏水。
（四）设计原因
1、坡屋面变坡交接处、老虎窗与屋面连接处等，由于受力钢筋配置不足，不能满足板块支座弯矩应力而开裂，导致渗漏。
2、构造设计不当，如为追求建筑形式，将泛水高度降低过多，导致屋面连接处、屋面与墙身连接处的防水高度低于暴雨瞬时积水高度，造成女儿墙渗漏。另外，外檐沟断面尺寸过小、雨水口的间距过大等也能造成坡屋面的渗漏。
3、设计时的设防原则与实际存在差异，比如设计配筋时，一般仅考虑结构承重，而不考虑屋面的温度变形，对混凝土产生温度裂缝预估不足。
三、混凝土坡屋面渗漏的防治对策
（一）严格控制材料的质量
钢筋、水泥、骨料、保温材料、防水材料及屋面瓦等材质的优劣直接影响到屋面的防水效果，严禁使用不合格产品。
钢筋一般用 Φ4冷拔低碳钢丝，间距一般为100～200mm。
水泥一般采用普通硅酸盐或硅酸盐水泥，标号不低于32.5R，主要指标须符合要求。从降低水化热及水泥用量的角度，可采用掺合粉煤灰的水泥。
针对屋面板较薄且钢筋较密的特点，粗骨料宜采用10～20mm的碎石，含泥量不大于 1%；细骨料宜采用 M=2.8的中粗砂，含泥量不大于3%。
适当添加外加剂，可大大提高混凝土结构层自身防水功能。适合坡屋面的外加剂有无机铝盐防水剂（BS2型），它同时具有防水剂、膨胀剂、减水剂和缓凝剂4种功能，能提高混凝土致密性和强度，防水效果好，其掺量一般为水泥质量的3%。
混凝土配合比应先经过试验确定，水灰比及混凝土搅拌时间应严格控制，水灰比不大于 0.55，水泥用量不应少于330kg/m3；应根据施工季节和屋面倾角，选择最佳坍落度。
保温材料重点是控制材料的密度，一般坡屋面保温层采用聚苯乙烯板，密度不小于 18kg/m3。
按防水材料的不同，防水层可分为柔性防水和刚性防水。柔性防水用防水卷材，如高聚物改性沥青卷材；刚性防水则为水泥砂浆结合高分子防水涂料，如丙烯酸酯防水涂料。
屋面瓦优先选择性能好、尺寸规整的波形瓦，避免施工时扣口不严密、留缝大等隐患。
（二）確保施工的质量
1、模板和钢筋工程
使用双面支模法，配置双层模板，使用止水螺杆加固。加强整个坡屋面模板支撑的连接，形成满堂脚手，增大抗倾力矩，以防坡屋面混凝土浇筑时产生的水平分力作用使屋面走模变形，同时防止混凝土漏浆和后期凿打。做好水电管路、避雷带等的预埋工作。
坡屋面混凝土工程
做好施工组织，合理安排混凝土搅拌、运输和浇捣时间，搅拌采用滚动式搅拌机。浇筑混凝土时，以屋檐为起点，以1500 mm（单面支模）或 1000 mm（双面支模）宽自下而上逐层浇筑，并设置 500 mm宽的挡板以免浇筑时骨料滑落。浇筑施工段以屋脊为界，左右两边同时向中间展开。
对于双面支模屋面，宜采用小型振动棒按序插振，防止漏振，对无法振动的部位应采用板外振、人工插捣等方式；对于单面支模屋面，可选择机械振捣与人工敲打相结合。振捣宜自下向上进行，且不宜过快，一般应振捣2～3遍。
尽量减少施工缝的留设，无法避免时，也尽量留设在结构受力最小的部位；施工缝处继续浇筑混凝土时，应先清除水泥薄膜和松动石子，湿润并冲净后再浇筑，老混凝土和新混凝土相接处采用高标号水泥砂浆浇接。
防水层施工
屋面板基层清理干净并充分湿润后，施工20mm厚1:3水泥砂浆找平层，每立方米砂浆掺入1kg麻丝随机搅拌，以防开裂，用铁抹子反复压实赶光。结构变坡、交角部位，抹成半径50mm的圆弧形。
屋面板防水施工前，必须在屋面变坡交接处、老虎窗与屋面连接处及墙身泛水、排气井根部、檐沟等部位，以及结构复杂的排水集中部位做防水附加增强层，即在板交接缝两侧各300mm宽范围内增刷3遍聚合物水泥防水涂料，并加一层玻纤布增强。
4、屋面瓦施工
在绑扎屋面瓦前，应作一层内敷钢筋网的细石混凝土保护层。屋面瓦应采用坐浆挤压法贴实，要求灰浆挤满瓦缝，以防波瓦空鼓。施工前基层板面洒水湿润，瓦片充分吸水待用；施工时用 1∶2.5 水泥砂浆铺贴波瓦，并用 Φ0.8 铜丝与保护层外露钢筋扎牢。按要求做好泛水、屋面变坡等部位的瓦面搭接。
细部处理
（1）檐口
防水层与檐沟交接处设凹槽，防水层收头压入槽内钉牢，用密封材料封固，水泥砂浆抹压。钉子四周用嵌缝膏密封，外露部分压入保护层内。
（2）泛水
也在交接处留凹槽，防水层收头压入凹槽，用金属压条钉压，用密封材料封固端头，水泥砂浆抹压。
（3）穿过防水层的管道
管道与基层交接处预留20 mm×20mm的槽，用性能较好的密封材料填充，管道四周找平层按要求放坡，防水层与管道绑牢并密封封口。
（4）阴阳角、屋脊、天沟
一般基层需用水泥砂浆做成圆角或钝角，便于防水层施工，同时可涂刷2mm厚密封材料或高分子卷材作为附加层。
（三）提高设计质量
优秀的防水设计是确保防水工程质量的前提，设计应根据屋面防水等级来确定相应的防水标准，并根据“防排结合、刚柔并济，多道防线、共同作用”的原则来确定设防构造。
参考现行钢筋混凝土设计规范，考虑屋面板与板、板与梁的相互影响，合理地假设结构形式。设计应保证结构有足够刚度，尽量减少屋面板的挠度，设置足够负弯钢筋，提高抗裂性。
应力集中区、转角及容易出现渗漏的细节部位，须进行构造设计，并有详图及说明。
结语
综上，钢筋混凝土坡屋面的防渗效果与设计、选材及施工都密切相关，要提高屋面的防渗质量，必须从这 3 方面同时入手，三重把关。设计遵循“防排结合、刚柔并济，多道设防、共同作用”的大原则，注意细部构造。要合理选用性能优良的钢筋、水泥、骨料、保温材料、防水材料及屋面瓦等材料，控制混凝土的配合比，适当添加外加剂。支模、钢筋架设、混凝土浇筑养护及各构造层施工时都应遵循一定的工艺，细部结构的防渗须严格把关，保证施工质量，减少或杜绝坡屋面的渗漏。
参考文献
[1]李滨.薄板坡屋面防渗技术[J].科技资讯，2006.3.
[2]徐桂英.多层住宅坡屋面渗漏原因分析及改进措施[J].科技信息，2008.9.
[3]周忠义.防排结合，重视排水治理屋面渗漏[J].中国建筑防水，2010.4.
关键词：坡屋面；渗漏；结构；防水材料；模板
Abstract: the roof according to their grade generally can be divided into flat roof and slope roof, which because of the large slope, slope roofing roofing not easy seeper, roof sun Angle is large, rich facade is beautiful wait for a characteristic, is widely used in recent years. But some slope roof in the completion, or in the use of one or two years later, often happen leakage, leakage of parts for roofing junction, gable side, the place such as gun groove, affect the normal use of buildings and beautiful. This article mainly concrete slope roof leakage causes and countermeasures for the further discuss.
Key words: slope roof; Leakage; Structure; Waterproof material; The template
中圖分类号： TV697.3+2 文献标识码：A文章编号：2095-2104(2013)
坡屋面的构造特点
目前最常用的是大面积现浇钢筋混凝土坡屋面，一般其从下至上大致可分为：结构层、找平层、防水隔热层、屋面瓦等4大构造层，各构造层的质量好坏都与屋面渗漏与否密切相关。
（一）结构层
现浇钢筋混凝土板，是屋面的主体结构。屋面防水效果的关键就在于结构层能否起到防水作用，混凝土的施工质量、是否密实、有否裂缝及钢筋架设是否合理等都直接影响屋面的防水效果。
（二）找平层
用以找平结构，形成坚硬平整表面，以便防水隔热层的施工，找平层施工时的质量好坏，将直接影响到防水隔热层的质量。
（三）防水隔热层
其实是隔热层和防水层2层，质量与各自的施工工艺及材料好坏有很大关系，如果质量不佳产生裂缝会导致屋面渗漏。
（四）屋面瓦
贴于坡屋面外表面，起到美化立面及防水、防渗作用。若瓦片抗渗、抗冻、吸水等性能不佳，尺寸控制不严，瓦接缝不严等都会造成屋面渗漏。
混凝土坡屋面的渗漏原因分析
（一）构造原因
坡屋顶形式多样、结构复杂，变坡转折处、结构交接面和细部节点比较多。对屋面板来说，这些都是支座部位，其实际受力情况因该处构造的不同而复杂多样，结构设计计算时假定的约束形式与实际存在一定的差异，而且，各面受力变形情况不一致，会导致交接处的应力集中，设计配置的构造钢筋往往不能抵抗该处板块受力产生的弯矩而发生了裂缝。同时，这些部位的防水设防施工困难，不同防水材料的性能差异使交接处的节点处理难度加大，增大屋面渗水的可能性。
（二）材料原因
1、混凝土
混凝土是一种非均匀材料，内部分布着大量的微小孔隙；材性上其抗拉强度较低，受拉时易出现裂缝；屋面露天受气候影响大，易热胀冷缩产生温度裂缝；屋面板在长期使用中发生徐变，也会引起结构裂缝，这些都易形成渗水通道。
2、防水材料
防水材料的选择也至关重要。当屋面坡度较大时，使用防水卷材施工不方便，容易下滑；节点细部采用卷材防水块材较小、搭接面多，无法保证枯贴质量。而在一些屋面板交接面变形较大，局部需要增设防水加强层，而此处使用防水涂膜施工层次较多，湿作业施工容易造成涂料流淌，施工进度慢，难以保证加强层厚度。
屋面瓦
屋面瓦是直接与雨水和大气接触的层面，若施工中瓦的材质不保证，存在砂眼裂缝孔洞现象；或者瓦片在常年的日晒雨淋作用下产生微细裂纹，会使瓦片本身的防水能力下降甚至丧失。此外，屋面瓦块体铺设的接缝太多，施工中不能保证瓦层的整体性，尤其在暴风雨和台风时易发生渗漏。
（三）施工原因
1、混凝土坍落度控制不当
坍落度过小，影响施工操作，混凝土不易振实，造成屋面渗漏；坍落度过大，混凝土内部多余水分蒸发后会形成微小空隙，容易连通形成毛细孔隙，成为雨水渗入的通道。
施工缝位置留设不当
若将施工缝留设在屋脊、屋面变坡处等结构应力转换处，容易产生裂缝。
细部处理欠妥
坡屋面往往形式较复杂、交接面多、节点多，这些部位钢筋绑扎及混凝土振捣都较困难，而且属于应力集中区域，施工不好则会使混凝土开裂。另外，屋面常有一些如排风道、下水管、天沟等的附加设施，施工处理不好很容易引起渗漏。
施工方法不当
有些坡度大于 30°的屋面仍采用地板支模，易造成施工质量事故；局部板厚不满足要求会使结构出现裂缝；钢筋配置不到位，负筋易被踩低，无法与混凝土一起抵抗弯矩而使板产生裂缝。
房屋交付使用后安装太阳能等设施，容易破坏防水层，使屋面漏水。
（四）设计原因
1、坡屋面变坡交接处、老虎窗与屋面连接处等，由于受力钢筋配置不足，不能满足板块支座弯矩应力而开裂，导致渗漏。
2、构造设计不当，如为追求建筑形式，将泛水高度降低过多，导致屋面连接处、屋面与墙身连接处的防水高度低于暴雨瞬时积水高度，造成女儿墙渗漏。另外，外檐沟断面尺寸过小、雨水口的间距过大等也能造成坡屋面的渗漏。
3、设计时的设防原则与实际存在差异，比如设计配筋时，一般仅考虑结构承重，而不考虑屋面的温度变形，对混凝土产生温度裂缝预估不足。
三、混凝土坡屋面渗漏的防治对策
（一）严格控制材料的质量
钢筋、水泥、骨料、保温材料、防水材料及屋面瓦等材质的优劣直接影响到屋面的防水效果，严禁使用不合格产品。
钢筋一般用 Φ4冷拔低碳钢丝，间距一般为100～200mm。
水泥一般采用普通硅酸盐或硅酸盐水泥，标号不低于32.5R，主要指标须符合要求。从降低水化热及水泥用量的角度，可采用掺合粉煤灰的水泥。
针对屋面板较薄且钢筋较密的特点，粗骨料宜采用10～20mm的碎石，含泥量不大于 1%；细骨料宜采用 M=2.8的中粗砂，含泥量不大于3%。
适当添加外加剂，可大大提高混凝土结构层自身防水功能。适合坡屋面的外加剂有无机铝盐防水剂（BS2型），它同时具有防水剂、膨胀剂、减水剂和缓凝剂4种功能，能提高混凝土致密性和强度，防水效果好，其掺量一般为水泥质量的3%。
混凝土配合比应先经过试验确定，水灰比及混凝土搅拌时间应严格控制，水灰比不大于 0.55，水泥用量不应少于330kg/m3；应根据施工季节和屋面倾角，选择最佳坍落度。
保温材料重点是控制材料的密度，一般坡屋面保温层采用聚苯乙烯板，密度不小于 18kg/m3。
按防水材料的不同，防水层可分为柔性防水和刚性防水。柔性防水用防水卷材，如高聚物改性沥青卷材；刚性防水则为水泥砂浆结合高分子防水涂料，如丙烯酸酯防水涂料。
屋面瓦优先选择性能好、尺寸规整的波形瓦，避免施工时扣口不严密、留缝大等隐患。
（二）確保施工的质量
1、模板和钢筋工程
使用双面支模法，配置双层模板，使用止水螺杆加固。加强整个坡屋面模板支撑的连接，形成满堂脚手，增大抗倾力矩，以防坡屋面混凝土浇筑时产生的水平分力作用使屋面走模变形，同时防止混凝土漏浆和后期凿打。做好水电管路、避雷带等的预埋工作。
坡屋面混凝土工程
做好施工组织，合理安排混凝土搅拌、运输和浇捣时间，搅拌采用滚动式搅拌机。浇筑混凝土时，以屋檐为起点，以1500 mm（单面支模）或 1000 mm（双面支模）宽自下而上逐层浇筑，并设置 500 mm宽的挡板以免浇筑时骨料滑落。浇筑施工段以屋脊为界，左右两边同时向中间展开。
对于双面支模屋面，宜采用小型振动棒按序插振，防止漏振，对无法振动的部位应采用板外振、人工插捣等方式；对于单面支模屋面，可选择机械振捣与人工敲打相结合。振捣宜自下向上进行，且不宜过快，一般应振捣2～3遍。
尽量减少施工缝的留设，无法避免时，也尽量留设在结构受力最小的部位；施工缝处继续浇筑混凝土时，应先清除水泥薄膜和松动石子，湿润并冲净后再浇筑，老混凝土和新混凝土相接处采用高标号水泥砂浆浇接。
防水层施工
屋面板基层清理干净并充分湿润后，施工20mm厚1:3水泥砂浆找平层，每立方米砂浆掺入1kg麻丝随机搅拌，以防开裂，用铁抹子反复压实赶光。结构变坡、交角部位，抹成半径50mm的圆弧形。
屋面板防水施工前，必须在屋面变坡交接处、老虎窗与屋面连接处及墙身泛水、排气井根部、檐沟等部位，以及结构复杂的排水集中部位做防水附加增强层，即在板交接缝两侧各300mm宽范围内增刷3遍聚合物水泥防水涂料，并加一层玻纤布增强。
4、屋面瓦施工
在绑扎屋面瓦前，应作一层内敷钢筋网的细石混凝土保护层。屋面瓦应采用坐浆挤压法贴实，要求灰浆挤满瓦缝，以防波瓦空鼓。施工前基层板面洒水湿润，瓦片充分吸水待用；施工时用 1∶2.5 水泥砂浆铺贴波瓦，并用 Φ0.8 铜丝与保护层外露钢筋扎牢。按要求做好泛水、屋面变坡等部位的瓦面搭接。
细部处理
（1）檐口
防水层与檐沟交接处设凹槽，防水层收头压入槽内钉牢，用密封材料封固，水泥砂浆抹压。钉子四周用嵌缝膏密封，外露部分压入保护层内。
（2）泛水
也在交接处留凹槽，防水层收头压入凹槽，用金属压条钉压，用密封材料封固端头，水泥砂浆抹压。
（3）穿过防水层的管道
管道与基层交接处预留20 mm×20mm的槽，用性能较好的密封材料填充，管道四周找平层按要求放坡，防水层与管道绑牢并密封封口。
（4）阴阳角、屋脊、天沟
一般基层需用水泥砂浆做成圆角或钝角，便于防水层施工，同时可涂刷2mm厚密封材料或高分子卷材作为附加层。
（三）提高设计质量
优秀的防水设计是确保防水工程质量的前提，设计应根据屋面防水等级来确定相应的防水标准，并根据“防排结合、刚柔并济，多道防线、共同作用”的原则来确定设防构造。
参考现行钢筋混凝土设计规范，考虑屋面板与板、板与梁的相互影响，合理地假设结构形式。设计应保证结构有足够刚度，尽量减少屋面板的挠度，设置足够负弯钢筋，提高抗裂性。
应力集中区、转角及容易出现渗漏的细节部位，须进行构造设计，并有详图及说明。
结语
综上，钢筋混凝土坡屋面的防渗效果与设计、选材及施工都密切相关，要提高屋面的防渗质量，必须从这 3 方面同时入手，三重把关。设计遵循“防排结合、刚柔并济，多道设防、共同作用”的大原则，注意细部构造。要合理选用性能优良的钢筋、水泥、骨料、保温材料、防水材料及屋面瓦等材料，控制混凝土的配合比，适当添加外加剂。支模、钢筋架设、混凝土浇筑养护及各构造层施工时都应遵循一定的工艺，细部结构的防渗须严格把关，保证施工质量，减少或杜绝坡屋面的渗漏。
参考文献
[1]李滨.薄板坡屋面防渗技术[J].科技资讯，2006.3.
[2]徐桂英.多层住宅坡屋面渗漏原因分析及改进措施[J].科技信息，2008.9.
[3]周忠义.防排结合，重视排水治理屋面渗漏[J].中国建筑防水，2010.4.