It has been found from the analysis of X-ray diffraction and the observation of TEM that the metastable ordered orthorhombic martensite phase in the rapidly solidified Ti3Al-2Nb alloy transforms to various phases at different aging temperatures. When the alloy aged at temperature of 500℃ for 20 min, the phase decomposition into B2 and O phases is related to the stressin the alloy. When the aged temperature above 600℃, the phase transforms to α2 phase by both shearing and chemical ordering
It has been found from the analysis of X-ray diffraction and the observation of TEM that the metastable ordered orthorhombic martensite phase in the rapidly solidified Ti3Al-2Nb alloy transforms to various phases at different aging temperatures. When the alloy aged at temperature of 500 ° C for 20 min, the phase decomposition into B2 and O phases is related to the stressin the alloy. When the aged temperature above 600 ° C, the phase transforms to α2 phase by both shearing and chemical ordering