【摘 要】
：
小型氨厂为了回收到品位较高的氨合成反应余热,就要提高合成塔出口气体温度.当合成塔出口温度超过200℃时,考虑材质耐氢腐蚀性能,不能采用碳钢,通常选用低合金珠光体耐热钢,
论文部分内容阅读
小型氨厂为了回收到品位较高的氨合成反应余热,就要提高合成塔出口气体温度.当合成塔出口温度超过200℃时,考虑材质耐氢腐蚀性能,不能采用碳钢,通常选用低合金珠光体耐热钢,如15Cr Mo、12Cr Mo等.这种钢的淬硬倾向较大,焊接时在焊缝和热影响区容易出现硬而脆的马氏体组织,这不但使焊接接头金属塑性降低、脆性的增
Small ammonia plant in order to recover high grade ammonia synthesis reaction waste heat, it is necessary to increase the gas temperature at the outlet of the synthesis tower.When the synthesis tower outlet temperature exceeds 200 ℃, considering the material resistance to hydrogen corrosion, carbon steel can not be used, usually low alloy Pearlite heat-resistant steel, such as 15Cr Mo, 12Cr Mo, etc. This kind of steel tends to harden harden and it is easy to appear hard and brittle martensite in the weld and heat affected zone during welding, which not only makes the welding joint metal Decreased plasticity, increased brittleness
其他文献
用极谱法测定硫氰酸铅络合物的各级稳定常数,结果如次:K_1=6.03,K_2=9.77,K_3=9.27,K_4=8.34,K_5=7.26,K_6=4.30(25℃,用高氯酸纳维持μ=3).又用同法测定硫氰酸锌络合物的各
This paper studies the buffer planning problem for interconnect-centric floorplanning for nanometer technologies. The dead-spaces are the spaces left unused wit
西部大开发是在我国国民经济经历了20多年的改革开放和发展的条件下提出来的，对於促进我国社会、经济发展和国家长治久安有着十分重大的意义。然而，由於我国西部幅员辽阔，基础较
师专公共英语课教学浅议樊永前在改革开放的今天，英语发挥着越来越重要的作用。我们培养的人才，不但要有一定的专业智能，而且要有一定的英语智能，这样才能有一定的竞争力，就业的路
〔教学目标〕培养学生的改革开放意识 ,认识发展对外经济关系对我国现代化建设的重要意义 ,从而树立为我国现代化建设贡献力量的远大志向。使学生明确实行对外开放是经济国际
本文指出任何僅含兩個常數的氣態方程,在臨界點附近的缺點是特別顯著的。同時也指出,對應態定律應用到高密度氣體的偏差,可以相當滿意地用臨界係數(?)來衡量。因此我們建議將
苏联E.O.巴顿电焊研究所已解决了在碳钢和不锈钢,钼和钽上电渣堆焊铜和铜合金(铝青铜、黄铜、青铜)问题。堆焊时采用ANM-11或ANM-12等高效焊剂,同时控制熔池的温度,不熔化被
本文用毛细上升法测定了四种脂肪醇(C_1—C_4)和四种脂肪酸(C_1—C_4)的水溶液在不同温度下的表面张力,计算了各种醇和酸的分子自溶液内部至表面的吸附热力学量,包括吸附自由
钢丝经过连续炉加热后立即进入铅槽等温淬火,以求获得均勾一致的索氏体组织。长5～7米,温度400～550℃的铅槽表面须覆盖保温材料,其目的是防止热量辐射,隔绝空气和铅液作用,避免
本钢种节铬无镍或少镍,在60℃以下全浓度硝酸中显示优良的耐蚀性,铸锻件在浓硝酸生产中可取代长期沿用的Cr23、Эи654,在稀硝酸生产中可代替1Cr18Ni9Ti,使用寿命比Cr23提高