Different oxygen and nitrogen containing functional groups were created on the surface of the multiwalled carbon nanotubes.The multi-walled carbon nanotubes were treated in ultrasonic bath with sulfuric or nitric acid.Furthermore the surface texture was m
【机 构】
：
Max Planck Institute for Chemical Energy Conversion, Stiftstrafβe 34-36, 45470 Mülheim an der Ruhr,
论文部分内容阅读
Different oxygen and nitrogen containing functional groups were created on the surface of the multiwalled carbon nanotubes.The multi-walled carbon nanotubes were treated in ultrasonic bath with sulfuric or nitric acid.Furthermore the surface texture was modified by increase of the roughness.In particular after treatment with the oxidizing nitric acid,in comparison to the H2SO4 or ultra-sonic treated samples,craters and edges are dominating the surface structures.Manganese oxide was deposited on the multiwalled carbon nanotubes by precipitation mechanism.Various manganese oxides are formed during the deposition process.The samples were characterized by elemental analysis,microscopy,thermal analysis,Raman spectroscopy,and by the zeta potential as well as X-ray diffraction measurements.It was shown that the deposited manganese oxides are stabilized rather by surface texture of the multi-walled carbon nanotubes than by created functional groups.
其他文献
MoS2 is a promising anode material for sodium ion batteries owing to its two-dimensional layered structure and high specific capacity.But it still exhibits a poor cycle stability and limited rate capability for Na storage because of its poor electrical co
Aluminum-ion batteries (AIBs) are attracting great attentions recently because of the high volumetric capacity,natural abundance of Al and operational safety.Using metallic Al as anode,the development of suitable cathode materials is a key issue to build
N-doped coaxial CNTs@α-Fe2O3@C nanofibers have been successfully synthesized according to a facile solvothermal/hydrothermal method.The obtained CNTs@α-Fe2O3@C nanofibers composites exhibited special three-dimensional (3-D) network structure,which endows
Use of metallic Li anode raises serious concerns on the safety and operational performance of Li-S batteries due to uncontrolled hazard of Li dendrite formation,which is difficultly eliminated as long as the metallic Li exists in the cells.Pairing lithium
Fe3-xO4 raspberry shaped nanostructures/graphene nanocomposites were synthesized by a one-step polyol-solvothermal method to be tested as electrode materials for Li-ion battery (LIB).Indeed,Fe3-xO4raspberry shaped nanostructures consist of original orient
V-doped SBA-16 catalysts (V-SBA-16) with 3D nanocage mesopores have been successfully synthesized by a modified one-pot method under weak acid condition.The obtained materials were characterized by means of small angle XRD,N2 adsorption-desorption,TEM,UV-
The Ni2P/MgAlO catalysts with different MgO/Al2O3 ratios were prepared by the phosphidation of corresponding Ni/MgAlO catalysts with triphenylphosphine in liquid phase.It was found that the MgO/Al2O3 ratio affected the Ni2P/MgAlO catalysts significantly.T
CO2 capture with ionic liquids (ILs) has attracted many attentions,and most works focused on absorption ability at ambient temperatures,while seldom research was concerned at elevated temperatures.This not only limits the CO2 absorption application at ele
Highly porous nitrogen-doped carbon materials were synthesized by the carbonization of a low-cost porous covalent triazine polymer,PCTP-3,which had been synthesized by the AlCl3 catalyzed FriedelCrafts reaction of readily available monomers.The nature of
Elevated-temperature pressure swing adsorption is a promising technique for producing high purity hydrogen and controlling greenhouse gas emissions.Thermodynamic analysis indicated that the CO in H2-rich gas could be controlled to trace levels of below 10