Effect of W/Cu composite filler metals on the microstructure and mechanical properties of laser weld

来源 :China Welding | 被引量 : 0次 | 上传用户:nineoneone911
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Cracking in a laser weld of niobium to stainless steel occurred due to the formation of brittle,continuously distributed Nb-Fe intermetallic compounds.A crack-free joint,which had a tensile strength of 147 MPa,was obtained by using the W/Cu composite fill
其他文献
The microstructure and mechanical properties of friction stir welded 2.5 mm 7050-77451 aluminum alloy natural aging 72 h and 17 520 h were investigated,respecti
期刊
In this paper, the performance characteristics of ASTM A19Q S31803 and ASTM A1S2 F51 duplex stainless steel were introduced, and the weldabilities were analyzed
The microstructure and mechanical properties of steel/Al structure material produced by additive manufacturing(AM) was investigated in this work based on the co
As a means of surface modification process,metal surface nanocrystallization(MSN) has attracted widespread attention and enjoyed a great prospect.However,curren
期刊
The restraint intensity(RI) of the pipeline girth welding joint was investigated using finite element method and experimental method to predict the cold crackin
期刊
Microstructure of transient liquid phase ( TLP) diffusion bonded a third generation single crystal superalloy joint was investigated using scanning electron mic
Mo-Cu composite and Cr18-Ni8 stainless steel were brazed with Ni-Cr-P filler metal in a vacuum of 10-4 Pa and a Mo-Cu/Cr18-Ni8 joint was obtained. Microstructur
The inner hole parts played an oriented or supporting role in engineering machinery and equipment, which are prone to appear surface damages such as wear, strai
The 304 stainless steel strips were deposited one layer on carbon steel base metal by electroslag strip cladding(ESC) and submerged arc cladding(SAC),respective
The 30 mm thick ASTM4130 steel pipe was fabricated by gas tungsten arc welding and shielded metal arc welding under quenched and tempered conditions.Whereafter,