The effect of a sputtered Ti-48Al-8Cr-2Ag (at.pct) coating on the oxidation resistance of the cast Ti-46.5Al-5Nb (at.pct) alloy was investigated in air at 1000~1
In order to evaluate the interfacial reaction, a SiCf/Ti (TA1) composite was fabricated by a vacuum hot pressingmethod and then heat-treated in vacuum at 800℃
Oxide scale formation on a C-steel surface has been investigated using linear heating rates ranging from 0.1℃/min to 10℃/min at high temperatures. The studies
Superperiodic feature was observed by scanning tunneling microscopy (STM) on the surface of highly oriented pyrolyticlattice constant is 7.03 nm. For the superl