论文部分内容阅读
对空心玻璃微球(HGM)在高温充气过程中的表面形貌进行了研究.分析局部晶化出现的时间和条件,并通过其表面形貌、成分分析探究了其随时间的变化规律.研究结果表明:影响 HGM高温充气后表面形貌的因素主要有充气温度和充气压力;充气温度越高、压力越大表面形貌发生变化所需时间越短.导致表面形貌变化的本质原因是结晶分相,结晶成分主要由 Na,B等元素组成.HGM的表面结晶分相使其表面粗糙度大幅度升高,但随着脱离充气环境后放置时间的延长而又逐渐降低.其表面粗糙度降低的主要原因是 Na,B等元素的逆向迁移.“,”The morphology on the surface of hollow glass mircospheres(HGMs)in inflating process was investigated in this work.The experimental results indicate that the main factors influencing the surface of HGM include temperature and pressure, and higher temperature and pressure contributed to the formation of surface morphology.After the appearance of the erosion-like surface morphology,the surface roughness of HGMs increased significantly.However,after some time of storage,the surface roughness of HGMs decreased.The reason for erosion is crystallization and phase separation in essence.The components of crys-tal mainly consist of the elements of Na and B.The converse transfer of the elements of Na and B causes the decrease of surface roughness of HGMs.