The corrosion behavior of CoCrFeNiMox alloys was investigated in aqueous environments,NaCl and H2SO4 solutions,respectively,to simulate typical neutral and acidic conditions.The cyclic polarization curves in NaC1 and the potentiodynamic curves in H2SO4 cl
【机 构】
:
State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 7100
论文部分内容阅读
The corrosion behavior of CoCrFeNiMox alloys was investigated in aqueous environments,NaCl and H2SO4 solutions,respectively,to simulate typical neutral and acidic conditions.The cyclic polarization curves in NaC1 and the potentiodynamic curves in H2SO4 clearly reveal the beneficial effects of Mo and the detrimental effect of σ-phase on the corrosion resistance.The X-ray photoelectron spectroscopy results of CoCrFeNiMox alloys in H2SO4 solution indicate that Cr and Mo predominate the corroded surface of the alloys,where Mo primarily exists in the form of MoO3.
其他文献
Optimization of grain boundary engineering (GBE) process is explored in a Fe-20Cr-19Mn-2Mo-0.82 N high-nitrogen and nickel-free austenitic stainless steel,and its intergranular corrosion (IGC) property after GBE treatment is experimentally evaluated.The p
The inclination angle of the flake particle has a significant impact on the in-plane thermal conductivity of composites.The graphite flake/Al composites (50 vol%) with different inclination angles were fabricated via flake powder metallurgy,and the result
High-strength,corrosion-resistant,and lightweight Al-Mg alloys perform an important function in harsh coastal service environments.Corrosion resistance is generally inversely correlated with strength;hence,it is difficult to simultaneously optimize both.I
Ni-Mo-P coatings are obtained at the surface of ceramic substrate by electroless deposition using palladium as a surface catalyst.The influence of catalyst activation conditions on coatings\' properties was assessed by structural,morphological,electrica
Mg and its alloys are the lightest structural metals available and are extremely attractive for applications as lightweight components,particularly in the automobile,electronic,and aerospace industries.The global market for wrought Mg alloys has steadily
The microstructure,mechanical properties and corrosion behavior of Mg-2Zn-0.6Zr alloy under the as-cast and asextruded conditions were investigated.Microstructure analysis indicated the remarkable grain refinement by extrusion,as well as notable reduction
Machining,especially dry machining of titanium alloys,has been one of the most significant challenges for carbide cutting tools.In this study,aluminum-rich AlTiN coating,as well as TiA1SiN nanocomposite coating,were successfully employed for dry milling o
An M-coated Mg-8 mass% Li alloy rectangular bar was fabricated by hot extrusion,and then,it was hot-rolled into a thin sheet.The Al coating was uniform in thickness and had good bonding with the substrate during all the processing.This Alcoated Mg-Li allo
A new kind of Mg-2Zn-0.6Ca (wt%) alloy was fabricated by casting and hot extrusion as a high-ductility structural material.The extruded alloy exhibits a superior elongation of ~ 30%,yield strength of 130 MPa and ultimate tensile strength of 280 MPa along
In the electromagnetic induction-controlled automated steel teeming (EICAST) technology of ladle,the height and location of the blocking layer are critical factors to determine the structure size and installation location of induction coil.And,they are al