论文部分内容阅读
A series of solid electrolytes (Ce_(0.8)RE_(0.2))_(1-x)M_xO_(2-δ)(RE: Rare earth, M: Alkali earth) were prepared by sol-gel methods. XRD indicated that a pure fluorite phase was formed at 800℃. The synthesis temperature by the sol-gel methods was about 700℃ lower than by the traditional ceramic method. The electrical conductivity and impedance spectra were measured. XPS showed that the oxygen vacancy increased obviously by doping MO, thus, resulting in the increase of the oxygen ionic transport number and conductivity. The performance of ceria-based solid electrolyte was improved. The effects of RE_2O_3 and MO on the electrical properties were discussed. The conductivity and the oxygen ionic transport number of (Ce_(0.8)Sm_(0.2))_(1-0.05)Ca_(0.05)O_(2(?)δ) is 0.126 S·cm~(-1) and 0.99 at 800℃, respectively.