The effect of extrusion ratio on microstructures and mechanical properties of magnesium alloy AZ91D extruded tube at 430℃ has been studied. After the evolution of microstructure and mechanical properties of AZ91D during extrusion were studied, the following parameters were obtained: tensile strength reached the climax value of 306.9MPa and elongation peak value of 10.1% at an extrusion ratio of 7.125, and with the increase of the extrusion ratio to 7.45, yield strength reached a top value of 285.795MPa with decreased tensile strength and elongation. It was concluded that mechanical properties of magnesium alloys AZ91D could be enhanced by adjusting the extrusion ratio near recrystallization.
The effect of extrusion ratio on microstructures and mechanical properties of magnesium alloy AZ91D extruded tube at 430 ° C has been studied. After the evolution of microstructure and mechanical properties of AZ91D during extrusion were studied, the following parameters were obtained: tensile strength reached the climax value of 306.9 MPa and elongation peak value of 10.1% at an extrusion ratio of 7.125, and with the increase of the extrusion ratio to 7.45, yield strength reached a top value of 285.795 MPa with decreasing tensile strength and elongation. It was concluded that mechanical properties of magnesium alloys AZ91D could be enhanced by adjusting the extrusion ratio near recrystallization.