Iron oxide nanoparticles (IONPs) have been usually surface-modified by organic molecules with abundant hydroxyl groups t......
本文通过对荣华二采区10...
By adopting sodium silicate as a major material,SiO2 nanoparticles (size in 8-15nm) water-dispersiod was prepared by ion......
目的:制备骨靶向丹参素脂质体并研究其理化性质.方法:采用逆向蒸发法制备靶向性脂质体.透射电镜观察脂质体的形态,HPLC测定脂质体......
Atmospheric-pressure Air Plasma Treatment of Polyester Fabrics for Inkjet Printing with Pigment Inks
Without any preptocessing, palyester fabric has lower ability to hold on water and inks due to the smooth morphology of ......
依次用密胺（MA）、2,4-甲苯二异氰酸酯（TDI）对聚磷酸铵（APP）进行改性,并分别应用于低密度线性聚乙烯（LLDPE）中。分别用APP在水中的溶解度变......
By adopting sodium silicate as a major material,SiO2 nanoparticles (size in 8-15nm) water-dispersiod was prepared by ion......
以偶氮二异丁腈为反应物,采用自由基反应对多壁碳纳米管进行功能基化,并在碳纳米管上连接腈基官能团.以红外光谱法证实碳纳米管的......
在空气中于1000℃对Si3N4粉末进行表面氧化改性,研究其在水相体系中的分散性能。研究表明：经氧化后Si3N4物相主要为Si3N4,粉末表面......
层状硅酸盐具有类似于固体润滑材料MoS2、石墨等的层状结构。前期研究表明，δ相层状硅酸盐表现出较好的摩擦学性能。在此基础上，笔者......
应用溶剂萃取还原法制备了在有机相中稳定的纳米银流体.萃取剂Cyanex 302可实现在硝酸浓度小于4 mol/L条件下对银的萃取.通过对有......
采用共沉淀表面修饰法，制备了硬脂酸修饰LaPO_4和Ce／LaPO_4纳米微粒，用红外光谱仪、X射线衍射和透射电子显微镜对表面修饰纳米微粒的......
通过对纳米级多孔SiO2在水性介质中的分散试验，解决了纳米SiO2在水性介质的团聚问题，并研究了各因素对纳米SiO2水悬浮液稳定性的影响......
4-（1,1,3,3-四甲基）-丁基-2-羟基苯甲酸（C8SA）对纳米TiO2微粒进行了表面改性.通过高分辨透射电子显微镜（HRTEM）、傅立叶红外光谱仪（FT-IR）......
采用乙基纤维素对拉伸后的聚对苯二甲酸乙二酯纤维（PET）进行表面修饰，研究PET纤维被修饰后的结晶行为。在差示扫描量热仪（DSC）上进行非......
采用经过表面处理的氧化钙填充到聚乙烯（PE）中，制得CaO-PE薄膜，其力学性能达到国家标准．氧化钙填充量最高可达30％．研究发现：添加1％复合光敏......
通过控制四氯化钛（TiCl4）的水解速度,制备出水杨酸（SA）原位表面修饰的TiO2纳米颗粒（TiO2/SA）.通过X射线衍射仪（XRD）,高分辨透射电子显微镜（H......