  5. Influence of Modified Carbon Nanotubes on the Mechanical Behavior of Epoxy Resin

Influence of Modified Carbon Nanotubes on the Mechanical Behavior of Epoxy Resin

来源 :The 12th Asian Textile Conference (第12届亚洲纺织会议暨2013年纺织学术年会) | 被引量 : 0次 | 上传用户：zhanghui1860
【摘 要】
：
The multi-walled carbon nanotubes (MWCNTs) oxidized by the vitriol/nitric acid were modified by modified silane coupling agent (KH560) treated with DOPO (9, 10-dihydro-9-oxa-10-heteropoly philippine-1
【作 者】
：
Jie Zhang Xuefeng Lu Kejing Yu Kun Qian 
【机 构】
：
School of Textile and Clothing, Jiangnan University, Wuxi, China
【出 处】
：
The 12th Asian Textile Conference (第12届亚洲纺织会议暨2013年纺织学术年会)
【发表日期】
：
2013年2期
下载到本地 , 更方便阅读
下载此文 赞助VIP
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The multi-walled carbon nanotubes (MWCNTs) oxidized by the vitriol/nitric acid were modified by modified silane coupling agent (KH560) treated with DOPO (9, 10-dihydro-9-oxa-10-heteropoly philippine-10-oxide;DOPO-KH560) to obtain the chemical modified MWCNTs.
其他文献
Preparation and Characterization of Surface-Carboxylated Polyethylene Terephthalate Nanofibrous Mats
Polyethylene terephthalate (PET) nanofibers have been widely used in biomedical applications, especially in vascular graft fabrication due to their excellent mechanical properties and biostability.How
会议
Preparation and Ammonia-sensitive Property of Ag-PANI/PA6 Composite Nanofibers
Silver-polyaniline/polyamide 6 (Ag-PANI/PA6) composite nanofibers were prepared via the electrospinning process with a PA6/formic acid solution and the in-situ polymerization of PANI doped with HCl on
会议
Influence of Matrix Hydrophilicity on Drug Loading and Vitro Release Behavior of Tetracycline Hydroc
Poly (lactide-co-glycolide) (PLGA) nanofibers loaded with tetracycline hydrochloride were successfully prepared using an electrospinning process.
会议
Preparation and Photocatalytic Properties of Porous TiO2 Nanofibers
The PVP/TBT composite nanofibers consisting of Polyvinyl pyrrolidone (PVP), tetrabutyl titanate (TBT) and acetone as solvent were successfully fabricated by the technique of electrospunning, then poro
会议
Innovative Form-stable Phase Change Composite Nanofibers of Capric-lauric Acid and Polyethylene Tere
In the present work, capric acid (CA) and lauric acid (LA) were selected to prepare binary CA-LA eutectic by melt-blending, and then the composite nanofibers of capric-lauric acid/polyethylene terepht
会议
Fabrication and Characterization of Carbon-graphene Composite Nanofibers by Electrospinning
In this work, polyacrylonitrile(PAN) nanofibers containing graphene oxide(GO) are prepared by the electrospinning method, and carbon/graphene(C/G) composite nanofibers are obtained after subsequent he
会议
Study on Preparation and Mechanical Properties of PLA/nano Silica Melt-spun Fibers
The nano silica was surface modified by the silane coupling agent KH570.Then the modified nano silica was melt and mixed with PLA to form a composite material.
会议
Preparation of Nano-mineral Pigment Hematite Water Dispersion and Its Dyeing Research in Textile
The mineral pigment as inorganic pigment there is no affinity to fabrics, so nano-mineral pigment hematite water dispersion was prepared with poly(maleic anhydride-co-vinyl acetate) copolymer (PMV) an
会议
Electrospinning Preparation of Fe3O4/ Cellulose Acetate Magnetic Nanofibers
Fe3O4 nano-magnetic powder is added to the spinning solution of cellulose acetate, acetone / acetic acid as the solvent, use the electrospinning prepared magnetic Fe3O4/cellulose acetate nanocomposite
会议
Catalytic Ozonation of Phenol in Water by Nano-Gadolinium Oxide
The strong oxidation of ozone and the adsorption and catalytic properties of catalyst can be combined in catalytic ozonation, therefore it can solve the problem which the organic matter cannot be comp
会议