【摘 要】
：
In this study, the influence of fiber orientation on the flexural strength of ultra-highperformance fiber-reinforced concrete (UHPFRC) was examined.To this end, a circular UHPFRC panel measuring (φ) 1
【机 构】
：
Department of Civil Engineering, Gifu University, 1-1 Yanagido, Gifu, Japan
【出 处】
：
The 10th International Symposium on High Performance Concret
论文部分内容阅读
In this study, the influence of fiber orientation on the flexural strength of ultra-highperformance fiber-reinforced concrete (UHPFRC) was examined.To this end, a circular UHPFRC panel measuring (φ) 1,200 x 50 mm was cast from its center, and test specimens measuring 50 x 50 × 200 mm with 10 mm notches for three-point bending tests were cut from it with angles of O, 30, 60 and 90° between the specimen axis and the radial direction of the panel.After the bending test, fiber orientation on the ruptured surfaces of the specimens was observed.The flexural strengths of the specimens cut at angles of 60, 30 and 0° were 80,40 and 10% of that for the specimen cut at an angle of 90°.It was also found that the flexural strength of specimens cut from a rectangular panel cast from its center point depended on their original positions and orientation within the panel.Similar fiber orientation characteristics were found in the circular and rectangular panels.
其他文献
钕铁硼作为第三代稀土永磁材料，具有磁能积大、矫顽力强高等特点，广泛应用于信息工业、汽车工业、航天工业、工程机械等领域，是支撑现代产业的重要材料之一。随着钕铁硼材料应用需求的不断增大，所消耗的稀土量也逐渐占据了稀土总产量的半壁江山。
目前熔盐电解法制备稀土金属及其合金技术已经取得长足的发展。本文综述了电解制备稀土金属或合金过程的电化学研究的相关基础数据,对在氟化物熔盐体系中已经开展研究的8种稀土元素(La,Ce,Pr,Nd,Sm,Gd和Y)的研究现状、结果进行了总结。
金属钐是重要的稀土元素之一，是制备高性能稀土永磁材料、储氢材料、核控制材料等高技术材料必不可少的基础材料。目前，镧热还原蒸馏法是工业生产金属钐的唯一方法，属间歇生产，设备要求高、生产周期长、加工成本很高，因此，科技工作者一直在探索廉价金属钐生产工艺的可能性，其中熔盐电解法是生产稀土金属及合金最主要方法，其生产成本最低，但由于Sm的变价特性，工业上采用熔盐电解法制备金属钐及其合金一直未获得成功。
In this paper, two types of modified hydrotalcites (MHT) were incorporated into cement mortars with two dosage levels (replacing 5% and 10% cement by mass).Designated testing programme including stren
An experimental investigation on the variation of compressive strength, splitting tensile strength and fracture energy, with the ratios of water to binder (W/B) of ultra-high strength concretes, inclu
In order to reduce the semi prefabricated RC frame component weight, improving the ductility and durability of RC components, the U shape ultra high performance cementitious composites shell with comb
High strength concrete for the production of concrete railway sleepers was designed more than 20 years ago.The compressive strength of the concrete was very high from the start, but flexure strengths
Ultra-High Performance Fiber Reinforced Concrete (UHPFRC) presents remarkable mechanical and durability properties.Concretes can be considered as UHPFRC when compressive strength and direct tensile st
The purpose of this study was to reduce production costs for UHPFRC members by using a bundle of longitudinal reinforcement bars as a substitute for steel fiber.Experiments on the ductile behavior of
Ongoing research and development of ultra-high performance concrete (UHPC) in the Czech Republic has been utilized in design and implementation of light-weight segmental deck of the cable-stayed footb