Effect of Zn and Cu additions on the single-step and two-step aging processes of 5xxx series Al alloy have been systematically investigated.For the newly developed alloys, the Mg-Cu clusters are respo
【机 构】
:
State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing
【出 处】
:
15th International Conference on Aluminium Alloys(ICAA15)(第十
论文部分内容阅读
Effect of Zn and Cu additions on the single-step and two-step aging processes of 5xxx series Al alloy have been systematically investigated.For the newly developed alloys, the Mg-Cu clusters are responsible for the rapid age hardening during the single-step aging treatment at 180℃C for 1 h, whereas Mg-Zn clusters do not appear.
其他文献
In traditional AA designation, Al alloys have been designated based on main alloy elements.However, with modem alloy design tools such as computation aided alloy design, Al alloys could be developed b
Differential scanning calorimetry (DSC) measurement of the stored energy is commonly used in nanostructured metals and alloys produced by severe plastic deformation (SPD).In this study, an ultra-high
Al-Si matrix composites are widely used in rail transportation, automotive, aerospace and other fields owing to its high specific strength, specific stiffness, high wear resistance and corrosion resis
Aluminum matrix composites (AMCs) are widely used because they combine the advantages of the matrix and the reinforcement phase.To serve both function and structure purposes, it is desirable to proces
Macrosegregation refers to the variation of composition on a large scale across the whole cross section of casting.This defect can be very severe for large sized direct chill (DC)casting billets/ingot
Effect of micro-alloying of transition elements in the near eutectic Al-Si-Mg base alloy on dynamic precipitation of Mg2Si phase during hot-rolling and its impact to mechanical properties were investi
The precipitation process and resulted hardening responds of two as-cast Al-Sc-Zr and Al-Sc-Zr-Er alloys during post-solidification ageing were investigated, aiming at developing cost-effective alumin
Recycling of aluminium alloys for automobiles from whole life cycle perspective, which processes end-of-life automobile components that are made of aluminium alloys with disassembly, testing, regenera
Aluminium based composite materials with exhibiting magnetic properties were fabricated using a mixture of pure aluminium and ferrite powder via mechanical alloying (MA) and subsequently spark plasma
An orthogonal hardness test of 4 factors, the first order aging temperature (T1) and time (t1), and the secondary aging temperature (T2) and time (t2), with 3 levels was adopted to obtain a rapid agin