The relationship between the ballistic coefficient and the static mechanical properties of armor materials was studied. The results show that the ballistic coef
The stability of ultra-fine microstructure during tempering at 650℃ was investigated on a Nb-containing steel. The steel had undergone 5 passes controlled roll