摘要 [目的]进一步研究卷烟热塌陷现象的产生原理，验证卷烟热塌陷现象与抽吸方式之间的关系。[方法]采用不同的抽吸方式对卷烟进行热塌陷试验，分析了抽吸方式对热塌陷的影响，验证了在同等条件下，卷烟的热塌陷值与抽吸容量及抽吸间隔间的关系，同时讨论了能够影响卷烟热塌陷的几种可能性因素。[结果]试验表明，卷烟滤棒及烟支部分的热塌陷值均随着抽吸容量增加而增大；且卷烟的热塌陷值还会随着抽吸间隔的缩短而增大。[结论]研究可为人们正确选择抽吸方式，尽量避免卷烟热塌陷现象提供参考依据。
关键词 卷烟；热塌陷；抽吸方式；影响因素
中图分类号 S572 文献标识码 A 文章编号 0517-6611（2014）11-03360-03
Abstract [Objective]To further study the mechanism of hot collapse problem of fluecured tobacco and to verify the relationship between the hot collapse and the smoking mode. [Method] Using different smoking modes to test hot collapse of fluecured tobacco， analyze the effect of puff volume and puff pause on hot collapse， and discuss possible factors influencing hot collapse of fluecured tobacco. [Results] The results indicated that the hot collapse increased as the puff volume increased and the puff pause decreased. [Conclusion]The study can provide reference basis for people selecting correct smoking mode and avoiding fluecured tobacco hot collapse.
Key words Fluecured tobacco； Hot collapse； Smoking mode； Influencing factors
在卷烟的不断燃烧过程中，其硬度会逐渐减小，同时因夹持和抽吸动作会对其施加一定的压力，以致卷烟产生形状上的畸变，这种现象被称为卷烟的热塌陷。卷烟的热塌陷现象严重影响卷烟的外形美观，同时还会导致抽吸阻力变大，吸食困难。
影响卷烟热塌陷的因素有很多，其中，抽吸方式是一个非常重要的因素。于是，为了减轻卷烟的热塌陷现象，笔者通过采用不同的抽吸方式来对卷烟进行热塌陷试验，研究分析抽吸方式对热塌陷的影响。
1 材料与方法
1.1 热塌陷测试材料
使用某品牌同一批次卷烟作为试验样品，在GB/T 16447规定的条件下调节样品的含水率，调节时间最短为48 h。
将调节后的卷烟样品按照质量进行筛选，取50支调节后的样品称重，算出平均值，挑选出质量位于平均值±0.02 g范围内的卷烟样品，作为热塌陷测试的材料。
2.3 抽吸方式对热塌陷的影响原因分析
根据上述试验结果可以得出，抽吸方式对于卷烟的热塌陷现象有着较大的影响。可能造成这些影响的因素很多，下面针对几种典型的因素进行可能性分析。
首先，热量是热塌陷的一个重要影响因素。卷烟燃烧过程中，施加压力部位的温度应随着燃烧锥与施压位置的距离缩短而增大，从而热塌陷值越大。
其次，水汽对卷烟的热塌陷也有着很大影响。有相关研究证明，造成卷烟滤棒部分的热塌陷现象最重要的原因即是水汽。滤棒中水含量对于自身纤维含量的比重越大，热塌陷现象越剧烈。卷烟中的水汽随着抽吸过程逐渐积累，当卷烟燃烧至接近施压位置时，施压位置的水含量最高，于是，热塌陷值最大。
由此推论，抽吸容量较小时，抽吸过程中卷烟燃烧距离较短，而阴燃距离较长，而阴燃过程产生的水汽大部分散发到空气中，积累下到卷烟内部的较少。抽吸容量越大，通过抽吸过程积累在卷烟内的水分越多，致使热塌陷值较高，于是得到试验所得出的结果。
而抽吸间隔缩短，同样是增大了卷烟抽吸时间，减少阴燃时间，使卷烟中积累的水分含量增多，从而增大了热塌陷值。同时由于抽吸间隔缩短，同样长度的卷烟，抽吸口数也
会有明显的增加。
此外，卷烟的吸阻、卷烟纸的透气度等因素均可能会对热塌陷现象造成一定影响，有待进一步研究。
3 结论
卷烟抽吸过程中，卷烟烟体在各种因素作用下会产生一定程度的热塌陷现象，严重影响抽吸感受。
为了了解卷烟热塌陷现象的原理与影响因素，为滤棒与卷烟生产厂家改进生产工艺提供参考，笔者主要对卷烟抽吸过程中的热塌陷现象进行研究，利用试验验证了卷烟的抽吸方式对于热塌陷值的影响。试验证明，卷烟的热塌陷值随着抽吸容量的增加而增大，并与抽吸间隔成正比。
同时，该研究还对抽吸方式造成热塌陷值不同的原因进行了分析，探讨了热量与水分等可能影响卷烟热塌陷值的因素。
参考文献
[1] 湖北中烟工业责任有限公司.YCT 354-2010 卷烟和滤棒物理性能的测定 热塌陷[S].北京：中国标准出版社，2010.
[2] 宋旭艳，张华，李文璟，等.卷烟热塌陷的测试方法[J].烟草科技，2012（1）：5-9.
[3] STEPHEN W P，VALERIE T，GERALD D，et al.Limitations in the characterization of cigarette products using different machine smoking regimes[J].Regulatory Toxicology and Pharmacology，2010，58：501-515.
[4] CELANESE CORPORATION.The effect of cellulose acetate fiber and filter parameters on hot collapse[R].World Smoking Products.1985.Part 5.18.In Legacy Tobacco Documents Library Bates No.620972599/2657，1985：2-7.
[5] TAKASE K，MIYAKE A.A study of hot collapse in cigarettes during smoking[C]//44th Tobacco Chemists Research Conference.Winston Salem，North Carolina，USA，1990.
[6] STEPHEN W P，XAVIER C，MIGUEL R，et al.Some consequences of using cigarette machine smoking regimes with differentintensities on smoke yields and their variability[J].Regulatory Toxicology and Pharmacology，2011，59：293-309.
关键词 卷烟；热塌陷；抽吸方式；影响因素
中图分类号 S572 文献标识码 A 文章编号 0517-6611（2014）11-03360-03
Abstract [Objective]To further study the mechanism of hot collapse problem of fluecured tobacco and to verify the relationship between the hot collapse and the smoking mode. [Method] Using different smoking modes to test hot collapse of fluecured tobacco， analyze the effect of puff volume and puff pause on hot collapse， and discuss possible factors influencing hot collapse of fluecured tobacco. [Results] The results indicated that the hot collapse increased as the puff volume increased and the puff pause decreased. [Conclusion]The study can provide reference basis for people selecting correct smoking mode and avoiding fluecured tobacco hot collapse.
Key words Fluecured tobacco； Hot collapse； Smoking mode； Influencing factors
在卷烟的不断燃烧过程中，其硬度会逐渐减小，同时因夹持和抽吸动作会对其施加一定的压力，以致卷烟产生形状上的畸变，这种现象被称为卷烟的热塌陷。卷烟的热塌陷现象严重影响卷烟的外形美观，同时还会导致抽吸阻力变大，吸食困难。
影响卷烟热塌陷的因素有很多，其中，抽吸方式是一个非常重要的因素。于是，为了减轻卷烟的热塌陷现象，笔者通过采用不同的抽吸方式来对卷烟进行热塌陷试验，研究分析抽吸方式对热塌陷的影响。
1 材料与方法
1.1 热塌陷测试材料
使用某品牌同一批次卷烟作为试验样品，在GB/T 16447规定的条件下调节样品的含水率，调节时间最短为48 h。
将调节后的卷烟样品按照质量进行筛选，取50支调节后的样品称重，算出平均值，挑选出质量位于平均值±0.02 g范围内的卷烟样品，作为热塌陷测试的材料。
2.3 抽吸方式对热塌陷的影响原因分析
根据上述试验结果可以得出，抽吸方式对于卷烟的热塌陷现象有着较大的影响。可能造成这些影响的因素很多，下面针对几种典型的因素进行可能性分析。
首先，热量是热塌陷的一个重要影响因素。卷烟燃烧过程中，施加压力部位的温度应随着燃烧锥与施压位置的距离缩短而增大，从而热塌陷值越大。
其次，水汽对卷烟的热塌陷也有着很大影响。有相关研究证明，造成卷烟滤棒部分的热塌陷现象最重要的原因即是水汽。滤棒中水含量对于自身纤维含量的比重越大，热塌陷现象越剧烈。卷烟中的水汽随着抽吸过程逐渐积累，当卷烟燃烧至接近施压位置时，施压位置的水含量最高，于是，热塌陷值最大。
由此推论，抽吸容量较小时，抽吸过程中卷烟燃烧距离较短，而阴燃距离较长，而阴燃过程产生的水汽大部分散发到空气中，积累下到卷烟内部的较少。抽吸容量越大，通过抽吸过程积累在卷烟内的水分越多，致使热塌陷值较高，于是得到试验所得出的结果。
而抽吸间隔缩短，同样是增大了卷烟抽吸时间，减少阴燃时间，使卷烟中积累的水分含量增多，从而增大了热塌陷值。同时由于抽吸间隔缩短，同样长度的卷烟，抽吸口数也
会有明显的增加。
此外，卷烟的吸阻、卷烟纸的透气度等因素均可能会对热塌陷现象造成一定影响，有待进一步研究。
3 结论
卷烟抽吸过程中，卷烟烟体在各种因素作用下会产生一定程度的热塌陷现象，严重影响抽吸感受。
为了了解卷烟热塌陷现象的原理与影响因素，为滤棒与卷烟生产厂家改进生产工艺提供参考，笔者主要对卷烟抽吸过程中的热塌陷现象进行研究，利用试验验证了卷烟的抽吸方式对于热塌陷值的影响。试验证明，卷烟的热塌陷值随着抽吸容量的增加而增大，并与抽吸间隔成正比。
同时，该研究还对抽吸方式造成热塌陷值不同的原因进行了分析，探讨了热量与水分等可能影响卷烟热塌陷值的因素。
参考文献
[1] 湖北中烟工业责任有限公司.YCT 354-2010 卷烟和滤棒物理性能的测定 热塌陷[S].北京：中国标准出版社，2010.
[2] 宋旭艳，张华，李文璟，等.卷烟热塌陷的测试方法[J].烟草科技，2012（1）：5-9.
[3] STEPHEN W P，VALERIE T，GERALD D，et al.Limitations in the characterization of cigarette products using different machine smoking regimes[J].Regulatory Toxicology and Pharmacology，2010，58：501-515.
[4] CELANESE CORPORATION.The effect of cellulose acetate fiber and filter parameters on hot collapse[R].World Smoking Products.1985.Part 5.18.In Legacy Tobacco Documents Library Bates No.620972599/2657，1985：2-7.
[5] TAKASE K，MIYAKE A.A study of hot collapse in cigarettes during smoking[C]//44th Tobacco Chemists Research Conference.Winston Salem，North Carolina，USA，1990.
[6] STEPHEN W P，XAVIER C，MIGUEL R，et al.Some consequences of using cigarette machine smoking regimes with differentintensities on smoke yields and their variability[J].Regulatory Toxicology and Pharmacology，2011，59：293-309.