论文部分内容阅读
通过水热法制备粉体的实验观察到金红石、锐钛矿和а－Ａｌ２Ｏ３晶体的生长习性．采用配位多面体生长习性法则合理地解释了ＴｉＯ２和а－Ａｌ２Ｏ３的生长习性．其主要结果为а－Ａｌ２Ｏ３晶体的生长习性为平板｛０００１｝，其各晶面的生长速度为：Ｖ｛０００１｝＜Ｖ｛１１２３｝＜Ｖ｛０１１２｝＝Ｖ｛１１２０｝＜Ｖ｛０１１０｝。金红石的生长习性为柱状，其各晶面的生长速度为：Ｖ＜１１０＞＜Ｖ＜１００＞＜ Ｖ＜１０１＞＜ Ｖ＜００１＞＜ Ｖ＜１１１＞；锐钛矿的生长习性为四面体，其各晶面的生长速度为Ｋ＜０１０＞＝Ｖ＜００１＞＞Ｖ＜０１０＞＞Ｖ＜１１１＞．而ＰＢＣ理论很难合理地解释а－Ａｌ２Ｏ３晶体的生长习性．
The growth habit of rutile, anatase and а-Al2O3 crystals was observed experimentally by hydrothermal method. The growth habit of TiO2 and а-Al2O3 was explained reasonably by the rule of coordination polyhedron growth. The main result is that the growth habit of а-Al2O3 crystal is flat plate {0001}, the growth rate of each crystal plane is: V {0001} . The growth habit of anatase is tetrahedron , And the growth rate of each crystal plane is K <010> = V <001> V <010 >> V <111>. The PBC theory is difficult to reasonably explain the growth habit of а-Al2O3 crystals.