【摘 要】
：
本文研究了稀土金属镧（Ｌａ）对ＦｅｃｕＮｂＳｉＢ系软磁合金结构与性能的影响。结果表明：当Ｌａ含量为０．５ａｔ％时，纳米晶Ｆｅ（７３）Ｃｕ１Ｎｂ３Ｓｉ（１３．５）Ｂ９Ｌａ（０．５）合金经４７０℃×１ｈ晶化退火后具有最佳软磁性能，其起始磁导率μ（０．００１）为８．３×１０４，矫顽力Ｈｃ为０．７０Ａ／ｍ。过高或过低的Ｌａ含量均不利
论文部分内容阅读
本文研究了稀土金属镧（Ｌａ）对ＦｅｃｕＮｂＳｉＢ系软磁合金结构与性能的影响。结果表明：当Ｌａ含量为０．５ａｔ％时，纳米晶Ｆｅ（７３）Ｃｕ１Ｎｂ３Ｓｉ（１３．５）Ｂ９Ｌａ（０．５）合金经４７０℃×１ｈ晶化退火后具有最佳软磁性能，其起始磁导率μ（０．００１）为８．３×１０４，矫顽力Ｈｃ为０．７０Ａ／ｍ。过高或过低的Ｌａ含量均不利于提高合金软磁性能。
In this paper, the effect of rare earth metal lanthanum (La) on the structure and properties of FecuNbSiB soft magnetic alloys was studied. The results show that when La content is 0.5at%, the nanocrystalline Fe (73) Cu1Nb3Si (13.5) B9La (0.5) alloy has the best soft magnetic properties after being annealed at 470 ℃ for 1h, The initial permeability μ (0.001) was 8.3 × 10 4, and the coercive force Hc was 0.70 A / m. High or low La content are not conducive to improve the soft magnetic properties of alloys.
其他文献
目的:考察牛黄清痔栓的主要药效作用及急性毒性。方法:通过体外抗菌试验、二甲苯致耳廓肿胀法、醋酸致局部溃疡法、热板镇痛法、小鼠断尾出血时间测定法考察牛黄清痔栓的抗菌
杂志微信、微博平台的开通,线下多姿多彩的主题论坛的举办,都是《中关村》杂志在新旧媒体的融合道路上所做的尝试。9月18日,2014中国期刊交易博览会在武汉启幕。来自40多个国
改革开放以来,我国学者在古代官箴研究领域(含对国外汉学家的翻译文献)积累了一定成果。主要表现在两大方面,一是与官箴有关的论文处于不断深化当中。二是官箴书的整理、研究
北京有关专家透露，中国已为西部大开发战略的启初订出四大优惠政策：１．国家把利用外资指标的６０％拨给西部；２．允许西部城市设立基础设施建设彩票；３．扩大地方企业发行债券的规模；４、尝试在西部成
本研究以诱导性的纸笔测试为基础,以大学非英语专业的学习者为研究对象,重点考察英语中介语使用过程中动词突显度和情状体两个语言因素对现在完成时标记的影响。研究结果表明
作者:[韩]金兰都(著)路冉(译)出版社:广西科学技术出版社推荐理由:在这本书中,我们知道了生活中的烦恼和悲伤是怎么形成的以及如何解决和化解这些烦恼与困感。作者把错综复杂
目的:探讨去乙酰化酶SIRT1基因多态性,与长期进行不同方式有氧运动的老年人高胆固醇血症的关联性。方法:在上海市不同社区发放调查问卷,选取323名长期进行不同方式有氧运动锻
目的探讨前列腺萎缩后增生(PAH)的病理形态学特征和鉴别诊断。方法收集前列腺PAH标本11例,选择34βE12、p63、P504S、PSA和PSAP抗体检测,观察其病理形态学特点和免疫组化表达
加氢反应器是加氢炼油成套设备的心脏，它在高温、高压及富氢工况条件下运行，这类高温高压容器的制造技术要求不低于核容器。对于大型热壁加氢反应器，为了防止其内壁的高温氢及硫